Synthesis of highly sulfonated poly(arylene ether sulfone)s with sulfonated triptycene pendants for proton exchange membranes
文献类型：期刊论文
| 作者 | Gong FX ; Mao HC ; Zhang YW ; Zhang SB ; Xing W |
| 刊名 | polymer
 |
| 出版日期 | 2011 |
| 卷号 | 52期号:8页码:1738-1747 |
| 关键词 | FUEL-CELL APPLICATIONS MULTIBLOCK COPOLYMERS ACID GROUPS POLYMER POLYIMIDE |
| ISSN号 | 0032-3861 |
| 通讯作者 | zhang sb |
| 中文摘要 | a series of poly(aryl ether sulfone)s containing triptycene groups pes-x-tpd (x refers to molar percentage of tpd) were firstly synthesized through nucleophilic aromatic substitution polycondensation by using 2,5-triptycenediol (tpd), bis(4-hydroxyphenyl) sulfone (bhps) and 4,4'-difluorodiphenyl sulfone (dfdps). the sulfonation of copolymers was conducted at room temperature by using a mild sulfonating reagent (98% h(2)so(4)), and the degree of sulfonation was readily and accurately controlled by adjusting the ratio of tpd and bhps. the structures of pes-x-tpd and spes-x-tpd were characterized by ir, (1)h nmr and (13)c nmr spectra. these ionomers generally showed high thermal stability and mechanical strength at low humidity regardless of high iec value. meanwhile, it is noteworthy that these novel spes-x-tpd membranes with high iec value achieved high proton conductivity in a wide range of humidity at 80 degrees c. for example, spes-60-tpd with the highest iec value 2.86 mmol/g displays the conductivity of 2.5 x 10(-1) s/cm which is much higher than that of the perfluorinated nafion membrane (1.1 x 10(-1) s/cm) at 80 degrees c and 94% rh. at 80 degrees c and 34% rh, spes-60-tpd displays the conductivity of 4.5 x 10(-3) s/cm which is also higher than that of the nafion membrane (3.0 x 10(-3) s/cm). microscopic analyses revealed that well-defined phase separated structures and uniform ionic pathway was formed for spes-45-tpd membrane with the iec of 2.29 mmol/g. moreover, a h(2)/o(2) fuel cell using the spes-55-tpd (iec = 2.68 mmol/g) also showed better performance than that of nafion 117 at 40 degrees c and 30% rh. (c) 2011 elsevier ltd. all rights reserved. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000289182800006 |
| 公开日期 | 2012-06-11 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/44712]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Gong FX,Mao HC,Zhang YW,et al. Synthesis of highly sulfonated poly(arylene ether sulfone)s with sulfonated triptycene pendants for proton exchange membranes[J]. polymer,2011,52(8):1738-1747. |
| APA | Gong FX,Mao HC,Zhang YW,Zhang SB,&Xing W.(2011).Synthesis of highly sulfonated poly(arylene ether sulfone)s with sulfonated triptycene pendants for proton exchange membranes.polymer,52(8),1738-1747. |
| MLA | Gong FX,et al."Synthesis of highly sulfonated poly(arylene ether sulfone)s with sulfonated triptycene pendants for proton exchange membranes".polymer 52.8(2011):1738-1747. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。