Synthesis and pH/Temperature-Responsive Behavior of PLLA-b-PDMAEMA Block Polyelectrolytes Prepared via ROP and ATRP
文献类型：期刊论文
| 作者 | Mao J ; Ji XL ; Bo SQ |
| 刊名 | macromolecular chemistry and physics
 |
| 出版日期 | 2011 |
| 卷号 | 212期号:7页码:744-752 |
| 关键词 | TRANSFER RADICAL POLYMERIZATION DIBLOCK COPOLYMER MICELLES AQUEOUS-SOLUTION DRUG-DELIVERY METHACRYLATE) POLYMERS MICELLIZATION COLLOIDS DESIGN CORES |
| ISSN号 | 1022-1352 |
| 通讯作者 | ji xl |
| 中文摘要 | well-defined diblock poly(l-lactide)-block-poly(dimethylamino-2-ethyl methacrylate) (plla-b-pdmaema) copolymers were synthesized by combining rop of lla and atrp of dmaema, from a dual-initiator 2-hydroxylethyl 2-bromoisobutyrate. the molecular characterization of these diblock copolymers was performed using (1)h nmr, ft-ir, and gpc-malls analysis. the responsive behavior of these diblock copolymers in aqueous solutions at different ph and temperatures were investigated using dls. results show that both higher ph and temperature result in a higher degree of neutralization, weaker hydrogen bonding, and micellar aggregation. as observed by tem, changes in micellar morphology are in accordance with dls results. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000288820500011 |
| 公开日期 | 2012-06-11 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/44739]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Mao J,Ji XL,Bo SQ. Synthesis and pH/Temperature-Responsive Behavior of PLLA-b-PDMAEMA Block Polyelectrolytes Prepared via ROP and ATRP[J]. macromolecular chemistry and physics,2011,212(7):744-752. |
| APA | Mao J,Ji XL,&Bo SQ.(2011).Synthesis and pH/Temperature-Responsive Behavior of PLLA-b-PDMAEMA Block Polyelectrolytes Prepared via ROP and ATRP.macromolecular chemistry and physics,212(7),744-752. |
| MLA | Mao J,et al."Synthesis and pH/Temperature-Responsive Behavior of PLLA-b-PDMAEMA Block Polyelectrolytes Prepared via ROP and ATRP".macromolecular chemistry and physics 212.7(2011):744-752. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。