Enhanced mechanical performance of poly(propylene carbonate) via hydrogen bonding interaction with o-lauroyl chitosan
文献类型：期刊论文
| 作者 | Qin YS ; Chen LJ ; Wang XH ; Zhao XJ ; Wang FS |
| 刊名 | carbohydrate polymers
 |
| 出版日期 | 2011 |
| 卷号 | 84期号:1页码:329-334 |
| 关键词 | HYPERBRANCHED POLYMER THERMAL-BEHAVIOR PROPYLENE-OXIDE BLENDS COPOLYMERIZATION COMPOSITES CATALYST DIOXIDE COMPLEX |
| ISSN号 | 0144-8617 |
| 通讯作者 | wang xh |
| 中文摘要 | biodegradable poly(propylene carbonate) (ppc) was blended with o-lauroyl chitosan (ocs) by solution casting using chloroform as common solvent. ftir and xps confirmed hydrogen bonding interaction between ppc and ocs, which was saturated when ocs loading reached 20 wt%. because of the hydrogen bonding interaction, a 2-3 degrees c increase in glass transition temperature and a 5% improvement (46-53 degrees c) in weight loss temperature (t(5%)) were observed in the ppc/ocs blend with ocs loading of 10-20 wt%. the interaction was beneficial to improving the mechanical performance of ppc. the tensile strength, elongation at break, and young's modulus of the pure ppc film were 31 mpa, 3.8%, and 392 mpa, respectively. for the blend with 10 wt% ocs loading, the effect of toughening was so substantial that the maximum elongation at break increased twofold to 8.1% and young's modulus increased nearly threefold to 1014 mpa: the tensile strength and stress at break remained unchanged. (c) 2010 elsevier ltd. all rights reserved. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000287349500043 |
| 公开日期 | 2012-06-11 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/44821]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Qin YS,Chen LJ,Wang XH,et al. Enhanced mechanical performance of poly(propylene carbonate) via hydrogen bonding interaction with o-lauroyl chitosan[J]. carbohydrate polymers,2011,84(1):329-334. |
| APA | Qin YS,Chen LJ,Wang XH,Zhao XJ,&Wang FS.(2011).Enhanced mechanical performance of poly(propylene carbonate) via hydrogen bonding interaction with o-lauroyl chitosan.carbohydrate polymers,84(1),329-334. |
| MLA | Qin YS,et al."Enhanced mechanical performance of poly(propylene carbonate) via hydrogen bonding interaction with o-lauroyl chitosan".carbohydrate polymers 84.1(2011):329-334. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。