Porous Co(3)O(4) microcubes: hydrothermal synthesis, catalytic and magnetic properties
文献类型：期刊论文
| 作者 | Cao F ; Wang DQ ; Deng RP ; Tang JK ; Song SY ; Lei YQ ; Wang S ; Su SQ ; Yang XG ; Zhang HJ |
| 刊名 | crystengcomm
 |
| 出版日期 | 2011 |
| 卷号 | 13期号:6页码:2123-2129 |
| 关键词 | POLYOL-MEDIATED SYNTHESIS COBALT OXIDE COO NANOCRYSTALS MESOPOROUS CO3O4 THERMAL-DECOMPOSITION FACILE SYNTHESIS NANOWIRE ARRAYS NANOSTRUCTURES OXIDATION PARTICLES |
| ISSN号 | 1466-8033 |
| 通讯作者 | zhang hj |
| 中文摘要 | well-defined porous co(3)o(4) microcubes have been synthesized by a simple one-pot solvothermal method combined with subsequent calcination. the formation mechanism of the cube-like precursor was proposed based on the anisotropic intrinsic structure of coco(3). importantly, after thermal treatment, the cube-like morphology could be completely preserved. moreover, the thermal decomposition of the corresponding precursor led to the formation of porous structure. the effects of calcination temperature on the catalytic properties of co(3)o(4) samples were investigated and the results demonstrated that 600 degrees c was superior among three samples with the highest catalytic properties. additionally, as an antiferromagnetic material, the sample showed a certain degree of ferromagnetism under the external magnetic field. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| 公开日期 | 2012-06-12 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/45133]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Cao F,Wang DQ,Deng RP,et al. Porous Co(3)O(4) microcubes: hydrothermal synthesis, catalytic and magnetic properties[J]. crystengcomm,2011,13(6):2123-2129. |
| APA | Cao F.,Wang DQ.,Deng RP.,Tang JK.,Song SY.,...&Zhang HJ.(2011).Porous Co(3)O(4) microcubes: hydrothermal synthesis, catalytic and magnetic properties.crystengcomm,13(6),2123-2129. |
| MLA | Cao F,et al."Porous Co(3)O(4) microcubes: hydrothermal synthesis, catalytic and magnetic properties".crystengcomm 13.6(2011):2123-2129. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。