P-type Ca doped SrCu2O2 thin film: Synthesis, optical property and photovoltaic application
文献类型：期刊论文
| 作者 | Deng, ZH ; Tao, RH; Meng, G; Fang, XD; Zhao, YP; Zhou, S; Deng, ZH; Meng, G
|
| 刊名 | journal of alloys and compounds
 |
| 出版日期 | 2012 |
| 中文摘要 | p-type transparent conducting oxide sr0.9ca0.1cu2o2 (scco) films were prepared by pulsed laser deposition (pld) technique on glass and n-si (1 0 0) substrates. some critical experiment factors were investigated, and it was found that well-crystallized, single phase scco films could be obtained with the substrate temperature higher than 350 degrees c, and the crystallinity was improved with the increase of laser energy fluence. sr0.9ca0.1cu2o2/n-si (scco/n-si) heterojunction and prototype thin film solar cell were demonstrated respectively. diode characteristic in the current-voltage response was observed and the ideality factor (n) of the diode was 3.7. the obtained n value is larger than unity due to structural imperfections of the layer and interface states. a prototype thin film solar cell with the best solar cell performance exhibits an open-circuit voltage (v-oc) of 140 mv and a short-circuit current density (j(sc)) of 0.072 ma/cm(2) under irradiation of am1.5 and 100 mw/cm(2). (c) 2011 elsevier b.v. all rights reserved. |
| 学科主题 | 等离子体物理与核聚变研究 |
| 公开日期 | 2012-07-09 |
| 源URL | [http://ir.hfcas.ac.cn/handle/334002/5734]  |
| 专题 | 合肥物质科学研究院_中科院等离子体物理研究所 |
| 推荐引用方式 GB/T 7714 | Deng, ZH,Tao, RH,Meng, G,et al. P-type Ca doped SrCu2O2 thin film: Synthesis, optical property and photovoltaic application[J]. journal of alloys and compounds,2012. |
| APA | Deng, ZH.,Tao, RH.,Meng, G.,Fang, XD.,Zhao, YP.,...&Meng, G.(2012).P-type Ca doped SrCu2O2 thin film: Synthesis, optical property and photovoltaic application.journal of alloys and compounds. |
| MLA | Deng, ZH,et al."P-type Ca doped SrCu2O2 thin film: Synthesis, optical property and photovoltaic application".journal of alloys and compounds (2012). |
入库方式： OAI收割
来源：合肥物质科学研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。