Synthesis and characterization of chitosan-g-poly(acrylic acid)/sodiumhumatesuperabsorbent
文献类型:期刊论文
作者 | Wang Q(汪琴)![]() ![]() |
刊名 | Carbohydrate Polymers
![]() |
出版日期 | 2007 |
卷号 | 70期号:2页码:166-173 |
关键词 | Chitosan Sodiumhumate Superabsorbent Water absorbency Swelling behavior |
ISSN号 | 0144-8617 |
通讯作者 | 王爱勤 aqwang@licp.cas.cn |
中文摘要 | A novel chitosan-g-poly(acrylic acid)/sodiumhumate (CTS-g-PAA/SH) multifunctional superabsorbent was prepared by graft polymerization among chitosan, acrylic acid and sodiumhumate in aqueous solution, using N,N′-methylenebisacrylamide as a crosslinker and ammonium persulfate as an initiator. And the samples were further characterized by means of FTIR, SEM and TGA. The effect of polymerization variables, including reaction temperature, content of initiator, crosslinker and sodiumhumate, the weight ratio of acrylic acid to chitosan, on water absorbency were studied. The swelling rate in distilled water and the swelling behavior in various pH value solutions were also investigated. The result from FTIR spectra showed that chitosan and sodiumhumate participated in graft polymerization reaction with acrylic acid. The introduced sodiumhumate could enhance water absorbency and the content of 10 wt% sodiumhumate gave the best absorption (183 g g?1 in distilled water and 41 g g?1 in 0.9 wt% NaCl solution). |
学科主题 | 功能高分子 |
收录类别 | SCI |
资助信息 | 国家863计划项目(2006AA03Z0454);中国科学院“西部行动”项目(KGCX2-YW-501) |
语种 | 英语 |
公开日期 | 2012-09-02 |
源URL | [http://210.77.64.217/handle/362003/211] ![]() |
专题 | 兰州化学物理研究所_环境材料与生态化学研究发展中心 |
推荐引用方式 GB/T 7714 | Wang Q,Wang AQ. Synthesis and characterization of chitosan-g-poly(acrylic acid)/sodiumhumatesuperabsorbent[J]. Carbohydrate Polymers,2007,70(2):166-173. |
APA | 汪琴,&王爱勤.(2007).Synthesis and characterization of chitosan-g-poly(acrylic acid)/sodiumhumatesuperabsorbent.Carbohydrate Polymers,70(2),166-173. |
MLA | 汪琴,et al."Synthesis and characterization of chitosan-g-poly(acrylic acid)/sodiumhumatesuperabsorbent".Carbohydrate Polymers 70.2(2007):166-173. |
入库方式: OAI收割
来源:兰州化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。