Dynamic damage and failure in viscoplastic materials
文献类型：期刊论文
| 作者 | Zheng J(郑坚); Wang ZP
|
| 刊名 | Engineering Fracture Mechanics
 |
| 出版日期 | 1995 |
| 卷号 | 52期号:6页码:1065-& |
| 关键词 | Fracture Ductile Copper |
| ISSN号 | 0013-7944 |
| 通讯作者 | JIAN, Z (reprint author), CHINESE ACAD SCI,INST MECH,NON LINEAR MECH CONTINUOUS MEDIA LAB,BEIJING 100080,PEOPLES R CHINA. |
| 中文摘要 | In this paper, a dynamic damage model in ductile solids under the application of a dynamic mean tensile stress is developed. The proposed model considers void nucleation and growth as parts of the damage process under intense dynamic loading (strain rates epsilon greater than or equal to 10(3) s(-1)). The evolution equation of the ductile void has the closed form, in which work-hardening behavior, rate-dependent contribution and inertial effects are taken into account. Meanwhile, a plate impact test is performed for simulating the dynamic fracture process in LY12 aluminum alloy. The damage model is incorporated in a hydrodynamic computer code, to simulate the first few stress reverberations in the target as it spalls and postimpact porosity in the specimen. Fair agreement between computed and experimental results is obtained. Numerical analysis shows that the influence of inertial resistance on the initial void growth in the case of high loading rate can not be neglected. It is also indicated that the dynamic growth of voids is highly sensitive to the strain rates. |
| 类目[WOS] | Mechanics |
| 研究领域[WOS] | Mechanics |
| 关键词[WOS] | FRACTURE ; DUCTILE ; COPPER |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:A1995TJ14700009 |
| 公开日期 | 2009-08-03 ; 2010-08-20 |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/39176]  |
| 专题 | 力学研究所_力学所知识产出(1956-2008) |
| 推荐引用方式 GB/T 7714 | Zheng J,Wang ZP. Dynamic damage and failure in viscoplastic materials[J]. Engineering Fracture Mechanics,1995,52(6):1065-&. |
| APA | 郑坚,&Wang ZP.(1995).Dynamic damage and failure in viscoplastic materials.Engineering Fracture Mechanics,52(6),1065-&. |
| MLA | 郑坚,et al."Dynamic damage and failure in viscoplastic materials".Engineering Fracture Mechanics 52.6(1995):1065-&. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。