Characteristics of Pt/PbZr0.52Ti0.48O3/Pt and Au/PbZr0.52Ti0.48O3/YBa2Cu3O7-delta capacitors after gamma-ray irradiation
文献类型:期刊论文
作者 | Gao, J ; Zheng, L ; Song, Z ; Lin, C ; Zhu, D |
刊名 | EUROPEAN PHYSICAL JOURNAL-APPLIED PHYSICS |
出版日期 | 1999 |
卷号 | 8期号:2页码:105 |
ISSN号 | 1286-0042 |
英文摘要 | PbZr0.52Ti0.48O3 (PZT) and YBa2Cu3O7-delta (YBCO) thin films were fabricated by a pulsed laser deposition (PLD) method. The Pt/PZT/Pt ferroelectric capacitors were fabricated on silicon substrates while the Au/PZT/YBCO capacitors were fabricated on LaAlO3 substrates. The capacitance-voltage (C-V) properties and the hysteresis loops of the capacitors were measured before and after gamma-ray irradiation. The results show that for Pt/PZT/Pt capacitors, the remanent polarization P-r and the absolute coercive field E-C increase while the dielectric constant epsilon decrease with increasing accumulated dose. For the Au/PZT/YBCO capacitors, P-r and epsilon decreased with accumulated dose, but the absolute value of the negative and positive coercive fields increased. The results have been interpreted by radiation-induced positive charge trapping at defects in the ferroelectric materials. |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000084474200002 |
公开日期 | 2012-09-25 |
源URL | [http://ir.sinap.ac.cn/handle/331007/9896] |
专题 | 上海应用物理研究所_中科院上海原子核所2003年前 |
推荐引用方式 GB/T 7714 | Gao, J,Zheng, L,Song, Z,et al. Characteristics of Pt/PbZr0.52Ti0.48O3/Pt and Au/PbZr0.52Ti0.48O3/YBa2Cu3O7-delta capacitors after gamma-ray irradiation[J]. EUROPEAN PHYSICAL JOURNAL-APPLIED PHYSICS,1999,8(2):105. |
APA | Gao, J,Zheng, L,Song, Z,Lin, C,&Zhu, D.(1999).Characteristics of Pt/PbZr0.52Ti0.48O3/Pt and Au/PbZr0.52Ti0.48O3/YBa2Cu3O7-delta capacitors after gamma-ray irradiation.EUROPEAN PHYSICAL JOURNAL-APPLIED PHYSICS,8(2),105. |
MLA | Gao, J,et al."Characteristics of Pt/PbZr0.52Ti0.48O3/Pt and Au/PbZr0.52Ti0.48O3/YBa2Cu3O7-delta capacitors after gamma-ray irradiation".EUROPEAN PHYSICAL JOURNAL-APPLIED PHYSICS 8.2(1999):105. |
入库方式: OAI收割
来源:上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。