Preparation and characterization of porous TiO2 with La2O3 load
文献类型：期刊论文
| 作者 | Cao Linhong ; Qu Yufeng ; Xie Dongmei ; Jing Chuanyong |
| 刊名 | RARE METALS
 |
| 出版日期 | 2011-03-01 |
| 卷号 | 30页码:221—224 |
| 中文摘要 | The porous TiO2 were prepared by the sol-gel method and via urea-formaldehyde resins templates route from commercial TiOSO4. And porous TiO2 were sintered for 3 h at 500, 600, 700, 800 and 900 degrees C. The results show that the porous TiO2 is mainly composed of anatase TiO2 nanocrystals with a size of 10 similar to 50 nm and the crystalline size of TiO2 increases with increasing sintering temperature. Porous TiO2 with La2O3 load were fabricated by different molar content of La2O3 (2.5 mol.%, 5.0 mol.%, 7.5 mol.% and 10 mol.%) at a sintering temperature of 600 degrees C in order to prevent the crystal phase transformation of anatase to rutile. The surface of porous TiO2 loaded with La2O3 possessed a sponge-like structure with pores of about 1 similar to 2 mu m. The surface area of porous TiO2 with La2O3 load is at range from 70.1929 to 126.8309 m(2)/g. The sample has better properties than the other samples, owing to the large specific surface area (similar to 77.2539 m(2)/g) and the strong peaks of TiO2 and La2O3 for the sample with 7.5 mol.% La2O3. It may be applied to water pollution treatment in order to remove arsenic and fluorine simultaneously. |
| WOS记录号 | WOS:000303126300048 |
| 公开日期 | 2012-10-18 |
| 源URL | [http://ir.rcees.ac.cn/handle/311016/7099]  |
| 专题 | 生态环境研究中心_环境化学与生态毒理学国家重点实验室 |
| 推荐引用方式 GB/T 7714 | Cao Linhong,Qu Yufeng,Xie Dongmei,et al. Preparation and characterization of porous TiO2 with La2O3 load[J]. RARE METALS,2011,30:221—224. |
| APA | Cao Linhong,Qu Yufeng,Xie Dongmei,&Jing Chuanyong.(2011).Preparation and characterization of porous TiO2 with La2O3 load.RARE METALS,30,221—224. |
| MLA | Cao Linhong,et al."Preparation and characterization of porous TiO2 with La2O3 load".RARE METALS 30(2011):221—224. |
入库方式： OAI收割
来源：生态环境研究中心
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。