Tribological behaviors of diamond-like carbon coatings on plasma nitrided steel using three BN-containing lubricants
文献类型:期刊论文
作者 | Li B(李斌)![]() ![]() ![]() ![]() |
刊名 | Applied Surface Science
![]() |
出版日期 | 2009 |
卷号 | 255页码:6666-6674 |
关键词 | BN-containing additives Diamond-like carbon coating Tribology XPS |
ISSN号 | 0169-4332 |
通讯作者 | 夏延秋 |
中文摘要 | In this work, diamond-like carbon (DLC) coatings were deposited on plasma nitrided AISI 1045 steel by magnetron sputtering. Three BN-containing additives andmolybdenumdithiocarbamate (MoDTC) were added to poly-alpha-olefin (PAO) as additives. The additive content (mass fraction) in PAO was fixed at 0.5 wt%. The friction and wear characters of DLC coatings on nitrided steel discs sliding against AISI 52100 steel balls were tested under the lubricated conditions. It was found that borate esters have a higher load carrying capacity and much better anti-wear and friction-reducing ability than that of MoDTC. X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) were employed to explore the properties of the worn surface and the mechanism of friction and wear. According to the XPS analysis, the adsorbed organic N-containing compounds and BN are, possibly, the primary reason for the novel borate esters to possess a relatively constant coefficient of friction and lower wear rate. On the other hand, possibly, the MoDTC molecules break down during sliding and produce many Mo-oxides, and then the Mo-oxides destroy the DLC coating because of its sharp edge crystalline solid structure. After destroying the DLC coating, theMoDTC reactwithmetals and formMoS2 tribofilm, and decrease coefficient of friction of rubbing pairs. |
学科主题 | 材料科学与物理化学 |
收录类别 | SCI |
资助信息 | “Hundred Talents Program” of CAS;“973” program (2007CB607606) |
语种 | 英语 |
WOS记录号 | WOS:000264925400042 |
公开日期 | 2012-11-13 |
源URL | [http://210.77.64.217/handle/362003/2006] ![]() |
专题 | 兰州化学物理研究所_固体润滑国家重点实验室 |
通讯作者 | Xia YQ(夏延秋); Xia YQ(夏延秋) |
推荐引用方式 GB/T 7714 | Li B,Xia YQ,Xia YQ,et al. Tribological behaviors of diamond-like carbon coatings on plasma nitrided steel using three BN-containing lubricants[J]. Applied Surface Science,2009,255:6666-6674. |
APA | 李斌,夏延秋,夏延秋,&王鹏.(2009).Tribological behaviors of diamond-like carbon coatings on plasma nitrided steel using three BN-containing lubricants.Applied Surface Science,255,6666-6674. |
MLA | 李斌,et al."Tribological behaviors of diamond-like carbon coatings on plasma nitrided steel using three BN-containing lubricants".Applied Surface Science 255(2009):6666-6674. |
入库方式: OAI收割
来源:兰州化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。