NiAl matrix high-temperature self-lubricating composite
文献类型：期刊论文
| 作者 | Bi QL(毕秦岭) ; Bi QL(毕秦岭); Zhu SY(朱圣宇); Yang J(杨军); Liu WM(刘维民)
|
| 刊名 | Tribology Letters
 |
| 出版日期 | 2011 |
| 卷号 | 41页码:535-540 |
| 关键词 | NiAl matrix High temperature Self-lubricating composite Wear |
| ISSN号 | 1023-8883 |
| 通讯作者 | 毕秦岭 |
| 中文摘要 | A high-temperature self-lubricating composite NiAl–Cr–Mo–CaF2 was fabricated using the powder met- allurgy technique, and the tribological behavior of the composite at a wide range of temperatures (room temper- ature to 1000 C) was investigated. The results showed that the composite had a favorable friction coefficient of about 0.2 and an excellent wear resistance of about 1 9 10-5 mm3 N-1 m-1 at the high temperatures tested (800 and 1000 C). The excellent self-lubricating perfor- mance was attributed to the formation of the glaze film on the worn surface consisting mainly of CaCrO4 and CaMoO4 as high-temperature solid lubricants. |
| 学科主题 | 材料科学与物理化学 |
| 收录类别 | SCI |
| 资助信息 | the National Natural Science Foundation of China (51075383);the Innovation Group Foundation from NSFC (50721062);the National 973 Project (2007CB607601) |
| 语种 | 英语 |
| WOS记录号 | WOS:000287498400007 |
| 公开日期 | 2012-09-24 |
| 源URL | [http://210.77.64.217/handle/362003/849]  |
| 专题 | 兰州化学物理研究所_固体润滑国家重点实验室 |
| 通讯作者 | Bi QL(毕秦岭); Bi QL(毕秦岭) |
| 推荐引用方式 GB/T 7714 | Bi QL,Bi QL,Zhu SY,et al. NiAl matrix high-temperature self-lubricating composite[J]. Tribology Letters,2011,41:535-540. |
| APA | 毕秦岭,毕秦岭,朱圣宇,杨军,&刘维民.(2011).NiAl matrix high-temperature self-lubricating composite.Tribology Letters,41,535-540. |
| MLA | 毕秦岭,et al."NiAl matrix high-temperature self-lubricating composite".Tribology Letters 41(2011):535-540. |