Al2O3掺杂对MnCoNi系NTC热敏电阻材料性能的影响
文献类型：期刊论文
| 作者 | 黄霞; 姚金城 ; 常爱民; 刘力; 彭昌文
|
| 刊名 | 电子元件与材料
 |
| 出版日期 | 2011 |
| 卷号 | 30期号:7页码:25-28 |
| 关键词 | Al2O3掺杂 NTC热敏电阻 尖晶石 MnCoNi系 电稳定性 |
| ISSN号 | 1001-2028 |
| 其他题名 | effects of al2o3 doping on the properties of mnconi system ntc thermistor materials |
| 中文摘要 | 采用传统固相法制备了Co1.5 xMn1.2Ni0.3AlxO4(x=0,0.02,0.04,0.06)NTC热敏电阻材料。借助XRD、SEM和几种电性能测试手段,研究了Al2O3掺杂对MnCoNi热敏电阻材料相结构及电性能的影响。结果表明:随着Al2O3掺杂量的增加,MnCoNi热敏电阻材料的晶体结构不变,晶粒减小,电阻率和材料常数B值由339.07Ω·cm、3489.07K分别增加到3723.89Ω·cm、3956.80K,电学稳定性由1.65%提高至0.17%。 |
| 英文摘要 | Co_(1.5-x)Mn_(1.2)Ni_(0.3)Al_xO_4(x=0,0.02,0.04,0.06)NTC thermistor materials were prepared by the traditional solid-state reaction method.The effects of Al_2O_3 doping on the microstructure and electric properties of prepared materials were studied through XRD,SEM and several instruments for electrical properties characterization.The results indicate that Al_2O_3 doping shows little effect on the crystal structure of prepared materials.However,with increasing Al_2O_3 content,the grain size of the MnCoNi thermistor materials decreases,while the resistivity,material constant B value and electrical stability increase from 339.07Omega·cm,3 489.07 K and 1.65%to 3 723.89Omega·cm,3 956.80 K and 0.17%,respectively. |
| 学科主题 | Engineering (provided by Thomson Reuters) |
| 公开日期 | 2012-11-29 |
| 源URL | [http://ir.xjipc.cas.cn/handle/365002/1573]  |
| 专题 | 新疆理化技术研究所_新疆维吾尔自治区电子信息材料与器件重点实验室 新疆理化技术研究所_材料物理与化学研究室 |
| 作者单位 | 中国科学院新疆理化技术研究所；新疆电子信息材料与器件重点实验室;中国科学院研究生院 |
| 推荐引用方式 GB/T 7714 | 黄霞,姚金城,常爱民,等. Al2O3掺杂对MnCoNi系NTC热敏电阻材料性能的影响[J]. 电子元件与材料,2011,30(7):25-28. |
| APA | 黄霞,姚金城,常爱民,刘力,&彭昌文.(2011).Al2O3掺杂对MnCoNi系NTC热敏电阻材料性能的影响.电子元件与材料,30(7),25-28. |
| MLA | 黄霞,et al."Al2O3掺杂对MnCoNi系NTC热敏电阻材料性能的影响".电子元件与材料 30.7(2011):25-28. |
入库方式： OAI收割
来源：新疆理化技术研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。