SrCo1-xNixO3-δ陶瓷材料的微结构和电性能
文献类型：期刊论文
| 作者 | 兰玉岐; 妥万禄; 常爱民
|
| 刊名 | 功能材料与器件学报
 |
| 出版日期 | 2007 |
| 卷号 | 13期号:1页码:63-67 |
| 关键词 | SrCo1-xNixO3-δ NTC热敏电阻器 低温 |
| ISSN号 | 10074252 |
| 其他题名 | Microstructure and electrical properties of SrCo1 -xNixO3-δ ceramics |
| 中文摘要 | 研究了SrCo1-xNixO3-δ(0≤x≤0.10)陶瓷材料(x=0,0.02,0.05和0.10)的微结构和电性能。SrCo1-xNixO3-δ陶瓷样品的结构用XRD和SEM测试分析,用热敏电阻数据采集系统测试了样品在低温-196℃和-183℃下的阻值和热敏电阻常数B值。样品的电阻值和B值随含量x的增加而增大、烧结温度的升高和恒温时间的增加而减小。测试结果表明:SrCo1-xNixO3-δ陶瓷是一种预计可在-196℃以下使用,很有应用前景的低温热敏电阻材料。 |
| 英文摘要 | The microstructure and electrical properties of SrCo1-xNixO3-δ (0 [less-than or equal to] x [less-than or equal to] 0.10) ceramic were investigated (x = 0, 0.02, 0.05 and 0.10). The microstructure of SrCo1-xNixO3-δ Ceramics was studied by XRD and SEM. The electrical resistance and thermistor materials constant (B value) of samples were measured at low temperatures, such as -196°C and -183°C. The results show that the electrical resistance and the B value of samples increased with the increasing content x and decreased with the increasing sintering temperatures and the soaking time. The SrCo1-xNixO3-δ ceramics could be potentially applied at temperatures -196°C as NTC thermistor materials. |
| 公开日期 | 2012-11-29 |
| 源URL | [http://ir.xjipc.cas.cn/handle/365002/1966]  |
| 专题 | 新疆理化技术研究所_材料物理与化学研究室 |
| 作者单位 | 中国科学院新疆理化技术研究所;中国科学院研究生院 |
| 推荐引用方式 GB/T 7714 | 兰玉岐,妥万禄,常爱民. SrCo1-xNixO3-δ陶瓷材料的微结构和电性能[J]. 功能材料与器件学报,2007,13(1):63-67. |
| APA | 兰玉岐,妥万禄,&常爱民.(2007).SrCo1-xNixO3-δ陶瓷材料的微结构和电性能.功能材料与器件学报,13(1),63-67. |
| MLA | 兰玉岐,et al."SrCo1-xNixO3-δ陶瓷材料的微结构和电性能".功能材料与器件学报 13.1(2007):63-67. |
入库方式： OAI收割
来源：新疆理化技术研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。