The study on preparation and spectrum properties of SrS:Eu, Sm
文献类型：期刊论文
| 作者 | Liu Yan-Ping; Chen Zhao-Yang; Fan Yan-Wei; Ba Wei-Zhen; Du Yan-Zhao; Wang Jun-Hua |
| 刊名 | Yingxiang Kexue yu Guanghuaxue/Imaging Science and Photochemistry
 |
| 出版日期 | 2008 |
| 卷号 | 26期号:4页码:299-304 |
| ISSN号 | 16742974 |
| 中文摘要 | 采用碳还原法合成SrS:Eu,Sm,研究了灼烧温度及灼烧时间对样品发光性能的影响.通过X射线衍射(XRD)测试证明合成材料纯度较高,样品具有SrS的面心立方结构,晶格常数为0.601nm.样品的激发谱峰值在272、340、466nm处,荧光光谱的峰值在614nm处,光激励发光峰为608nm,光激励发光的光谱响应范围为800—1400nm. |
| 英文摘要 | SrS:Eu, Sm material was prepared by carbon reduction method. The effect of calcinations' temperature and time on luminescence intensity were studied. X-ray diffraction (XRD) tests prove that the synthetically materials have single phase and the samples prepared is with face-center cubic structure and the lattice parameter is 0.601 nm. The peak of sample excitation spectrum is at 272 nm, 340 nm, and 466 nm. The peak of fluorescence spectrum is at 603 nm. The photo-stimulation luminescence spectrum of peak is at 608 nm. The optical stimulated luminescence spectral response range is between 800 and 1400 nm. |
| 收录类别 | EI |
| 公开日期 | 2012-11-29 |
| 源URL | [http://ir.xjipc.cas.cn/handle/365002/2038]  |
| 专题 | 新疆理化技术研究所_材料物理与化学研究室 |
| 作者单位 | Xinjiang Technical Institute of Physics and Chemistry, Chinese Acad. of Sci., Urumqi 830011, China |
| 推荐引用方式 GB/T 7714 | Liu Yan-Ping,Chen Zhao-Yang,Fan Yan-Wei,et al. The study on preparation and spectrum properties of SrS:Eu, Sm[J]. Yingxiang Kexue yu Guanghuaxue/Imaging Science and Photochemistry,2008,26(4):299-304. |
| APA | Liu Yan-Ping,Chen Zhao-Yang,Fan Yan-Wei,Ba Wei-Zhen,Du Yan-Zhao,&Wang Jun-Hua.(2008).The study on preparation and spectrum properties of SrS:Eu, Sm.Yingxiang Kexue yu Guanghuaxue/Imaging Science and Photochemistry,26(4),299-304. |
| MLA | Liu Yan-Ping,et al."The study on preparation and spectrum properties of SrS:Eu, Sm".Yingxiang Kexue yu Guanghuaxue/Imaging Science and Photochemistry 26.4(2008):299-304. |
入库方式： OAI收割
来源：新疆理化技术研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。