Co-Mn-Ni-O热敏纳米粉体的制备及其特性
文献类型：期刊论文
| 作者 | 叶峰; 妥万禄; 巴维真 |
| 刊名 | 功能材料与器件学报
 |
| 出版日期 | 2003 |
| 卷号 | 9期号:4页码:377-380 |
| 关键词 | NTC热敏电阻 超微细粉体 纳米粉体 共沉淀法 尖晶石 |
| ISSN号 | 1007-4252 |
| 其他题名 | preparation and properties of nanometer powder for co-mn-ni-o thermistors |
| 中文摘要 | 采用液相共沉淀法用草酸作为沉淀剂制备了Co-Mn-Ni-O陶瓷热敏电阻纳米粉体,并采用综合热分析(TG、DTA)、X射线衍射(XRD)和扫描电子显微技术(SEM)对该法制备的粉体和对照粉体进行了综合表征,结果显示用该方法可以制备晶粒平均粒径在9nm左右、粉体颗粒形貌呈球形、颗粒粒径在50～100nm范围内、粒度分布范围较窄的Co-Mn-Ni-O三元系NTC热敏纳米粉体粉体,能够满足Co-Mn-Ni-O陶瓷热敏电阻对粉体的要求。 |
| 英文摘要 | Nanometer powder of Mn - Co - Ni oxides was prepared by using co - precipitation method with oxalic acid as precipitator, and it was tested and analyzed using TG^DTA^XRD^SEM technology. The result shows that the powder of Mn - Co -Ni oxide can be obtained with following properties: grain size about 9nm, near - spherical shape particle with diameter about 50 ~ lOOnm , narrow range of the particle distribution. And these properties meet the requirement for making Co - Mn - Ni - O NTC thermistors. |
| 学科主题 | Chemistry (provided by Thomson Reuters) |
| 公开日期 | 2012-11-29 |
| 源URL | [http://ir.xjipc.cas.cn/handle/365002/2182]  |
| 专题 | 新疆理化技术研究所_材料物理与化学研究室 |
| 作者单位 | 中国科学院新疆理化技术研究所；中国科学院研究生院 |
| 推荐引用方式 GB/T 7714 | 叶峰,妥万禄,巴维真. Co-Mn-Ni-O热敏纳米粉体的制备及其特性[J]. 功能材料与器件学报,2003,9(4):377-380. |
| APA | 叶峰,妥万禄,&巴维真.(2003).Co-Mn-Ni-O热敏纳米粉体的制备及其特性.功能材料与器件学报,9(4),377-380. |
| MLA | 叶峰,et al."Co-Mn-Ni-O热敏纳米粉体的制备及其特性".功能材料与器件学报 9.4(2003):377-380. |
入库方式： OAI收割
来源：新疆理化技术研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。