preparationoftrititanatenanotubeandtemobservation
文献类型：期刊论文
| 作者 | Huang C(黄琮)2; Zhang KJ(张开坚)2; Dang Z(党志)2; Li XJ(李新军)1
|
| 刊名 | journalofinorganicmaterials
 |
| 出版日期 | 2006 |
| 卷号 | 21期号:3页码:547 |
| ISSN号 | 1000-324X |
| 英文摘要 | Trititanate nanotubes were synthesized from rutile TiO2 via hydrothermal process. The influences of process parameters such as stirring, acid leaching and calcination temperature on formation and structure of nanotubes were observed by TEM. The results show that continuous stirring could improve the directional growth of TiO2 particles and formation of trititanate nanoflakes, and nanotubes are formed in the acid leaching process. It also reveals that 300 degrees C is the critical transformation temperature between nanotubes and long-stick crystalline column. The nanotubes synthesized under optimal condition are uniform and longer than 1 mu m, and the ratio of length to diameter is 125:1. |
| 语种 | 英语 |
| 源URL | [http://ir.giec.ac.cn/handle/344007/22486]  |
| 专题 | 中国科学院广州能源研究所 |
| 作者单位 | 1.中国科学院广州能源研究所 2.华南理工大学 |
| 推荐引用方式 GB/T 7714 | Huang C,Zhang KJ,Dang Z,et al. preparationoftrititanatenanotubeandtemobservation[J]. journalofinorganicmaterials,2006,21(3):547. |
| APA | 黄琮,张开坚,党志,&李新军.(2006).preparationoftrititanatenanotubeandtemobservation.journalofinorganicmaterials,21(3),547. |
| MLA | 黄琮,et al."preparationoftrititanatenanotubeandtemobservation".journalofinorganicmaterials 21.3(2006):547. |