Research on interfacial cracking of a Cr coating/steel substrate with and without laser pre-quenching treatment under thermal fatigue loading
文献类型：会议论文
| 作者 | Yang BQ(杨班权); Chen GN(陈光南) ; Chen XJ(陈学军); Sun WH; Chen HQ; Pan JW; Chen Y
|
| 出版日期 | 2012 |
| 会议名称 | 3rd International Conference on Digital Manufacturing and Automation, ICDMA 2012 |
| 会议日期 | AUG 01-02, 2012 |
| 会议地点 | Guangxi, China |
| 通讯作者邮箱 | yangbq1022@sina.com |
| 关键词 | Chromate coatings Chromium Manufacture Quenching Substrates Thermal fatigue Interfacial adhesions Interfacial cracking Loading condition Steel substrate Substrate surface |
| 卷号 | 190-191 |
| 页码 | 543-546 |
| 通讯作者 | 杨班权 |
| 中文摘要 | The interfacial cracking behaviors of a chromium (Cr) coating/laser pre-quenched steel substrate system and a Cr coating/original steel substrate system under thermal fatigue loading were investigated in this work. The experiment results show that the Cr coating on the pre-quenched substrate surface exhibited a higher resistance of interfacial cracking than that of the Cr coating on the original substrate surface under the same loading condition. This indicates the technology of laser pre-quenching of steel substrate surface prior to plating the Cr coating can improve the interfacial adhesion properties between the coating and substrate. |
| 收录类别 | CPCI-S ; EI |
| 合作状况 | 国内 |
| 产权排序 | 1 Division of Engineering Mechanics, Department of Mechanical Engineering, Academy of Armored Force Engineering, No. 21, Du-Jia-Kan, Chang-Xin-Dian, Beijing 100072, China 2 Laboratory of surface modification, Institute of mechanics, Chinese Academy of Sciences, No. 15 Bei-si-huan-xi Road, Beijing 100190, China 3 School of Applied Sciences, University of Science and Technology Beijing, No. 30 Xue-Yuan Road, Beijing 100083, China |
| 会议网址 | http://dx.doi.org/10.4028/www.scientific.net/AMM.190-191.543 |
| 会议录 | DIGITAL MANUFACTURING AND AUTOMATION III
 |
| 会议录出版者 | TRANS TECH PUBLICATIONS, P.O. BOX 1254, CLAUSTHAL-ZELLERFELD, D-38670, GERMANY |
| 语种 | 英语 |
| ISSN号 | 1660-9336 |
| WOS记录号 | WOS:000311978100117 |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/46842]  |
| 专题 | 力学研究所_先进制造工艺力学重点实验室 |
| 推荐引用方式 GB/T 7714 | Yang BQ,Chen GN,Chen XJ,et al. Research on interfacial cracking of a Cr coating/steel substrate with and without laser pre-quenching treatment under thermal fatigue loading[C]. 见:3rd International Conference on Digital Manufacturing and Automation, ICDMA 2012. Guangxi, China. AUG 01-02, 2012.http://dx.doi.org/10.4028/www.scientific.net/AMM.190-191.543. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。