FeAl-based coatings deposited by high-energy micro-arc alloying process for wet-seal areas of molten carbonate fuel cell
文献类型：期刊论文
| 作者 | P. Y. Guo ; C. L. Zeng ; N. Wang ; Y. Shao |
| 刊名 | Journal of Power Sources
 |
| 出版日期 | 2012 |
| 卷号 | 217页码:485-490 |
| 关键词 | Molten carbonate fuel cell Wet-seal area High-energy micro-arc alloying process Iron aluminide coating Corrosion Electrochemical impedance spectroscopy stainless-steel interconnects corrosion behavior separator plates reduction oxygen layer ni dy |
| ISSN号 | 0378-7753 |
| 中文摘要 | The corrosion of bipolar plates is a great obstacle to the industrial application of molten carbonate fuel cell (MCFC). No electrical conductivity is needed for the wet-seal materials, thus the application of aluminum coatings is a very effective method to inhibit the corrosion of wet-seal areas of MCFC by the formation of a protective Al2O3 scale. In this work, a high-energy micro-arc alloying (HEMAA) process is attempted to prepare FeAl coatings on the type 316 stainless steel (316SS) as wet-seal material of MCFC using an FeAl intermetallic compound rod as the deposition electrode. The microstructure of the FeAl coatings is analyzed, and its corrosion behavior in molten (0.62Li, 0.38K)(2)CO3 at 650 degrees C in air is examined by electrochemical impedance spectroscopy. The experimental results indicate that the FeAl coating on 316SS is microcrystalline, with a metallurgic bonding with the substrate. The Nyquist plots for the corrosion of both the bare and the coated steel are all composed of double capacitive loops, but with significantly larger impedance values observed for the coated steel. The FeAl coatings increase greatly the corrosion resistance of 316SS by forming a compact and adhesive Al2O3 scale. (C) 2012 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/59975]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | P. Y. Guo,C. L. Zeng,N. Wang,et al. FeAl-based coatings deposited by high-energy micro-arc alloying process for wet-seal areas of molten carbonate fuel cell[J]. Journal of Power Sources,2012,217:485-490. |
| APA | P. Y. Guo,C. L. Zeng,N. Wang,&Y. Shao.(2012).FeAl-based coatings deposited by high-energy micro-arc alloying process for wet-seal areas of molten carbonate fuel cell.Journal of Power Sources,217,485-490. |
| MLA | P. Y. Guo,et al."FeAl-based coatings deposited by high-energy micro-arc alloying process for wet-seal areas of molten carbonate fuel cell".Journal of Power Sources 217(2012):485-490. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。