Influence of dissolved oxygen concentration on the oxide film formed on 304 stainless steel in high temperature water
文献类型：期刊论文
| 作者 | W. J. Kuang ; X. Q. Wu ; E. H. Han |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2012 |
| 卷号 | 63页码:259-266 |
| 关键词 | Stainless steel SEM XPS Oxidation Oxide coatings stainless-steel 288-degrees-c water corrosion behavior hydrogenated water aqueous corrosion pourbaix diagrams mechanism zinc iron alloy-690 |
| ISSN号 | 0010-938X |
| 中文摘要 | Characteristics of the oxide films formed on 304 stainless steel under different dissolved oxygen (DO) concentrations in 290 degrees C water were investigated. Less hematite and more spinel oxides form on fresh sample as DO decreases. Meanwhile, relative Cr content in the film increases. Spinel develops on the film preformed under 3 ppm DO when it was further immersed under DO below 5 ppb while the preformed hematite degrades. The spinel preformed under DO below 5 ppb still grows up when further immersed under 3 ppm DO while the base layer becomes more porous due to dissolution of Cr. (C) 2012 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/60040]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | W. J. Kuang,X. Q. Wu,E. H. Han. Influence of dissolved oxygen concentration on the oxide film formed on 304 stainless steel in high temperature water[J]. Corrosion Science,2012,63:259-266. |
| APA | W. J. Kuang,X. Q. Wu,&E. H. Han.(2012).Influence of dissolved oxygen concentration on the oxide film formed on 304 stainless steel in high temperature water.Corrosion Science,63,259-266. |
| MLA | W. J. Kuang,et al."Influence of dissolved oxygen concentration on the oxide film formed on 304 stainless steel in high temperature water".Corrosion Science 63(2012):259-266. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。