Preparation of porous alumina ceramic with ultra-high porosity and long straight pores by freeze casting
文献类型：期刊论文
| 作者 | D. Y. Li ; M. S. Li |
| 刊名 | Journal of Porous Materials
 |
| 出版日期 | 2012 |
| 卷号 | 19期号:3页码:345-349 |
| 关键词 | Porosity Al2O3 Freeze casting Porous ceramic Tert-butyl alcohol channels |
| ISSN号 | 1380-2224 |
| 中文摘要 | Porous alumina ceramic was prepared by freeze casting method using tert-butyl alcohol as the solvent. The as-prepared porous alumina ceramic possessed long straight porous structure. The non-dendrite pore feature was quite distinguished from that prepared based on common solvents such as water and camphene. The porosity of the ceramic could be regulated through the solid loading. When the solid loading in the slurry was 20 vol%, the porosity of the alumina ceramic was 65%. With decreasing the solid loading, the porosity of the alumina ceramic increased linearly. The relationship between the total porosity (P) and initial solid loading (X) can be expressed as P = 98.8-17X. The ultra-high porosity of 82% could be achieved when the solid loading was 10 vol%. Moreover, the density of the porous alumina ceramic with the porosity of 82% was even lower than water's. The compressive strength of the porous alumina ceramic with the porosity of 63 and 82% was determined to be 37.0 and 2.6 MPa, respectively. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/60053]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | D. Y. Li,M. S. Li. Preparation of porous alumina ceramic with ultra-high porosity and long straight pores by freeze casting[J]. Journal of Porous Materials,2012,19(3):345-349. |
| APA | D. Y. Li,&M. S. Li.(2012).Preparation of porous alumina ceramic with ultra-high porosity and long straight pores by freeze casting.Journal of Porous Materials,19(3),345-349. |
| MLA | D. Y. Li,et al."Preparation of porous alumina ceramic with ultra-high porosity and long straight pores by freeze casting".Journal of Porous Materials 19.3(2012):345-349. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。