Phase formation and microstructure evolution of arc ion deposited Cr2AlC coating after heat treatment
文献类型：期刊论文
| 作者 | J. J. Li ; Y. H. Qian ; D. Niu ; M. M. Zhang ; Z. M. Liu ; M. S. Li |
| 刊名 | Applied Surface Science
 |
| 出版日期 | 2012 |
| 卷号 | 263页码:457-464 |
| ISSN号 | 0169-4332 |
| 关键词 | Cr2AlC Coating Cathodic arc deposition Microstructure n thin-films degrees-c m(n+1)ax(n) phases thermal-stability bulk cr2alc oxidation ti evaporation corrosion behavior |
| 中文摘要 | Due to the excellent oxidation and hot corrosion resistance and matched thermal expansion coefficient to normal alloys, Cr2AlC has potential applications as high-temperature protective coating. In the present work, the preparation of Cr2AlC coating has been achieved through cathodic arc deposition method combined with heat post-treatment. It was found that the coating, deposited from Cr2AlC compound target in the unintentional heating condition, was amorphous. After annealing at 620 degrees C in Ar for 20 h, the amorphous Cr-Al-C coating happened to crystallize and transformed to crystalline Cr2AlC as the major phase. It is obvious that the formation temperature of Cr2AlC was decreased from about 1050 degrees C for sintered bulk to around 620 degrees C for the as-deposited coating, resulting from the homogeneous mixture of the Cr, Al and C at atomic level in the Cr-Al-C coating. Apart from crystalline Cr2AlC, the annealed coating also contained AlCr2 and little Cr7C3. AlCr2 formed due to the loss of C during deposition, and little Cr7C3 always existed in the sintered Cr2AlC compound target as impurity phase. (C) 2012 Elsevier B. V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/60056]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. J. Li,Y. H. Qian,D. Niu,et al. Phase formation and microstructure evolution of arc ion deposited Cr2AlC coating after heat treatment[J]. Applied Surface Science,2012,263:457-464. |
| APA | J. J. Li,Y. H. Qian,D. Niu,M. M. Zhang,Z. M. Liu,&M. S. Li.(2012).Phase formation and microstructure evolution of arc ion deposited Cr2AlC coating after heat treatment.Applied Surface Science,263,457-464. |
| MLA | J. J. Li,et al."Phase formation and microstructure evolution of arc ion deposited Cr2AlC coating after heat treatment".Applied Surface Science 263(2012):457-464. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。