The effect of 0.4 wt.% Mn addition on the localized corrosion behaviour of zinc in a long-term experiment
文献类型：期刊论文
| 作者 | X. L. Shang ; B. Zhang ; E. H. Han ; W. Ke |
| 刊名 | Electrochimica Acta
 |
| 出版日期 | 2012 |
| 卷号 | 65页码:294-304 |
| 关键词 | Zn Mn addition Localized corrosion EPMA XRD XPS atmospheric corrosion alloy coatings protective ability runoff rates zn-co resistance products steel ni electrodeposition |
| ISSN号 | 0013-4686 |
| 中文摘要 | The corrosion performances of pure Zn and Zn-0.4Mn alloy exposed in marine environment (Qingdao, east of China) have been studied after exposure for three years. Pitting corrosion occurs on both pure Zn and Zn-0.4Mn with fewer and smaller pits on Zn-0.4Mn alloy as revealed by confocal scanning laser microscope (CSLM), which indicates that the addition of Mn can reduce the localized corrosion of Zn. Corrosion products formed on pure Zn and Zn-0.4Mn have been characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), scanning electron microscopy (SEM) and electron probe micro-analyzer (EPMA). The main crystalline phases identified by XRD are Zn-5(CO3)(2)(OH)(6), Zn4O4(OH)(6) and NaZn4Cl(OH)(6)SO4 center dot 6H(2)O. respectively. Small amounts of ZnO and Zn(OH)(2) are also found which mainly present on top surface of corrosion films as revealed by XPS. Combined results of XRD and EPMA disclose that Zn4SO4(OH)(6) and NaZn4Cl(OH)(6)SO4 center dot 6H(2)O are the main compounds inside the pits with Zn4SO4(OH)(6) locating at the pit bottom. The formation mechanism of corrosion products inside pits and the role of small Mn addition on localized corrosion of Zn have been discussed. (C) 2012 Published by Elsevier Ltd. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/60205]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. L. Shang,B. Zhang,E. H. Han,et al. The effect of 0.4 wt.% Mn addition on the localized corrosion behaviour of zinc in a long-term experiment[J]. Electrochimica Acta,2012,65:294-304. |
| APA | X. L. Shang,B. Zhang,E. H. Han,&W. Ke.(2012).The effect of 0.4 wt.% Mn addition on the localized corrosion behaviour of zinc in a long-term experiment.Electrochimica Acta,65,294-304. |
| MLA | X. L. Shang,et al."The effect of 0.4 wt.% Mn addition on the localized corrosion behaviour of zinc in a long-term experiment".Electrochimica Acta 65(2012):294-304. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。