Characterisation of rust formed on carbon steel after exposure to open atmosphere in Qinghai salt lake region
文献类型：期刊论文
| 作者 | J. Wang ; Z. Y. Wang ; W. Ke |
| 刊名 | Corrosion Engineering Science and Technology
 |
| 出版日期 | 2012 |
| 卷号 | 47期号:2页码:125-130 |
| 关键词 | Carbon steel Atmospheric corrosion SEM Rust layer low-alloy steels weathering steel protective ability corrosion products room-temperature mechanism iron reduction environment layers |
| ISSN号 | 1478-422X |
| 中文摘要 | The rust layer formed on carbon steel after 1 year exposure to Qinghai salt lake atmosphere was characterised by the following complementary techniques: X-ray diffraction, infrared transmission spectroscopy, scanning electron microscopy and energy dispersive X-ray. The crystalline components of the rust layers consisted primarily of beta-FeOOH, gamma-FeOOH and iowaite [Mg4Fe(OH)(8)OCl(center dot)4H(2)O]center dot delta-FeOOH, ferrihydrite and amorphous rust were also found. Most corrosion products were contained in the inner layer, while foreign particles were mainly distributed in the outer layer. Energy dispersive X-ray and linear scanning results indicated that Cl and Mg elements were rich in the whole rust layer, in which case they will have had an important influence on the corrosion process of carbon steel in the salt lake atmospheric conditions. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/60289]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. Wang,Z. Y. Wang,W. Ke. Characterisation of rust formed on carbon steel after exposure to open atmosphere in Qinghai salt lake region[J]. Corrosion Engineering Science and Technology,2012,47(2):125-130. |
| APA | J. Wang,Z. Y. Wang,&W. Ke.(2012).Characterisation of rust formed on carbon steel after exposure to open atmosphere in Qinghai salt lake region.Corrosion Engineering Science and Technology,47(2),125-130. |
| MLA | J. Wang,et al."Characterisation of rust formed on carbon steel after exposure to open atmosphere in Qinghai salt lake region".Corrosion Engineering Science and Technology 47.2(2012):125-130. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。