The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure
文献类型：期刊论文
| 作者 | J. Wang ; L. Z. Zhou ; L. Y. Sheng ; J. T. Guo |
| 刊名 | Materials & Design
 |
| 出版日期 | 2012 |
| 卷号 | 39页码:55-62 |
| 关键词 | Ferrous metals and alloys Heat treatments Microstructure single-crystal phase instabilities additions alloy |
| ISSN号 | 0261-3069 |
| 中文摘要 | The microstructure evolution and its influence on the mechanical properties are investigated in a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure. It is found that the tertiary gamma' phase disappears and the secondary gamma' phase coarsens and coalesces gradually, which acts as the main reason for the decreasing of strength at both room temperature and 900 degrees C. During exposure, the grain boundary coarsens from discontinuous to half-continuous and finally to continuous structure. The optimum half-continuous grain boundary structure composed of discrete M23C6 and M3B2 wrapped by gamma' film leads to the elongation peak at room temperature in the thermally exposed specimens. At 900 degrees C, the increase in the elongation is attributed to the much softer matrix and the formation of microvoids. The behavior of primary MC decomposition is a diffusion-controlled process. During exposure, various derivative phases including M23C6, gamma', eta, M6C and sigma sequentially form in the decomposed region. Primary MC decomposition and the precipitation of sigma phase have little effect on the mechanical properties due to their low volume fractions. (C) 2012 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/60291]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. Wang,L. Z. Zhou,L. Y. Sheng,et al. The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure[J]. Materials & Design,2012,39:55-62. |
| APA | J. Wang,L. Z. Zhou,L. Y. Sheng,&J. T. Guo.(2012).The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure.Materials & Design,39,55-62. |
| MLA | J. Wang,et al."The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure".Materials & Design 39(2012):55-62. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。