Influence of the characteristic of recrystallization grain boundary on the formation of creep cracks in a directionally solidified Ni-base superalloy

文献类型:期刊论文

作者G. Xie ; L. H. Lou
刊名Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
出版日期2012
卷号532页码:579-584
关键词Recrystallization Superalloy Cracks Dislocation Grain boundary surface recrystallization microstructure dislocations cmsx-4
ISSN号0921-5093
中文摘要Creep tests of a directionally solidified (DS) Ni-base superalloy specimens containing local recrystallization (RX) were carried out at 980 degrees C/235 MPa and the influence of the characteristic of RX grain boundary on the formation of creep cracks was investigated. The RX grain boundary morphology, misorientation and dislocation pattern at high, low angle and twin boundaries during creep were examined. It was shown that only a few high angle grain boundaries (GBs), but not all of them cracked during creep and even after ruptured. This is associated with the dislocation mobility at GBs or the morphology of CBs. The possibility of crack formation was discussed based on the transmission behavior of dislocations at different GBs. (C) 2011 Elsevier B.V. All rights reserved.
原文出处://WOS:000301160100080
公开日期2013-02-05
源URL[http://ir.imr.ac.cn/handle/321006/60352]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
G. Xie,L. H. Lou. Influence of the characteristic of recrystallization grain boundary on the formation of creep cracks in a directionally solidified Ni-base superalloy[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2012,532:579-584.
APA G. Xie,&L. H. Lou.(2012).Influence of the characteristic of recrystallization grain boundary on the formation of creep cracks in a directionally solidified Ni-base superalloy.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,532,579-584.
MLA G. Xie,et al."Influence of the characteristic of recrystallization grain boundary on the formation of creep cracks in a directionally solidified Ni-base superalloy".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 532(2012):579-584.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。