Boron-doped glassy carbon fabricated by chemical vapor deposition

文献类型:期刊论文

作者L. Xu ; J. F. Wu ; S. Bai
刊名New Carbon Materials
出版日期2012
卷号27期号:3页码:226-232
关键词Boron Glassy carbon Chemical vapor deposition Microstructure catalytic graphitization films
ISSN号1007-8827
中文摘要A boron-doped glassy carbon was fabricated by chemical vapor deposition from a gaseous CH4/BCl3 mixture. It was characterized by X-ray diffraction, Raman spectroscopy, scanning, and transmission electron microscopy. Results show that the deposited carbon is characteristic of a glass-like carbon but with boron carbide nanocrystals around 20 nm in diameter uniformly distributed in its matrix. In contrast to the conventional non-graphitizable glassy carbon, the product behaved similarly to a graphitizable carbon on high-temperature treatment because of the strong catalytic graphitization effect of the boron. The glass carbon was transformed into lamellar carbon structures, probably by a dissolution-precipitation mechanism.
原文出处://WOS:000306351200011
公开日期2013-02-05
源URL[http://ir.imr.ac.cn/handle/321006/60370]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
L. Xu,J. F. Wu,S. Bai. Boron-doped glassy carbon fabricated by chemical vapor deposition[J]. New Carbon Materials,2012,27(3):226-232.
APA L. Xu,J. F. Wu,&S. Bai.(2012).Boron-doped glassy carbon fabricated by chemical vapor deposition.New Carbon Materials,27(3),226-232.
MLA L. Xu,et al."Boron-doped glassy carbon fabricated by chemical vapor deposition".New Carbon Materials 27.3(2012):226-232.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。