Electrochemical preparation of NiAl intermetallic compound from solid oxides in molten CaCl2 and its corrosion behaviors in NaCl aqueous solution
文献类型：期刊论文
| 作者 | H. Y. Yin ; T. Yu ; D. Y. Tang ; X. F. Ruan ; H. Zhu ; D. H. Wang |
| 刊名 | Materials Chemistry and Physics
 |
| 出版日期 | 2012 |
| 卷号 | 133期号:1页码:465-470 |
| 关键词 | Corrosion test Nickel aluminide Electrochemical reduction Molten salt electrolytic reduction 3-phase interlines calcium-chloride insulator compounds hydrogen-production alloy decomposition methane salts mo |
| ISSN号 | 0254-0584 |
| 中文摘要 | Nickel aluminide powders were prepared by direct electrochemical reduction of solid mixture of NiO-NiAl2O4 (Ni:Al = 1:1 in mol) precursor in molten CaCl2 at 850 degrees C. The reduction process of the solid oxide cathode was investigated by analyzing the intermediate products using X-ray diffraction (XRD) and scanning electron microscopy (SEM). It reveals that nickel is preferentially reduced and it benefits to prevent aluminum leaving from the cathode. The products obtained at the constant cell voltage electrolysis of 3.0 V for more than 4 h were stoichiometric NiAl. The energy consumption could be as low as 6.1 kWh (kg-NiAl)(-1) based on the applied cell voltage and the consumed electrolysis charge. Furthermore, the NiAl powders were made into a dense rod by spark plasma sintering (SPS) technique. The corrosion behaviors of the NiAl rod in 0.5 mol L-1 NaCl aqueous solution at room temperature were investigated by polarization curve and ac impedance measurements. It was found that the NiAl rod had satisfactory anti-corrosion ability in the solution. (C) 2012 Elsevier BM. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/60416]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | H. Y. Yin,T. Yu,D. Y. Tang,et al. Electrochemical preparation of NiAl intermetallic compound from solid oxides in molten CaCl2 and its corrosion behaviors in NaCl aqueous solution[J]. Materials Chemistry and Physics,2012,133(1):465-470. |
| APA | H. Y. Yin,T. Yu,D. Y. Tang,X. F. Ruan,H. Zhu,&D. H. Wang.(2012).Electrochemical preparation of NiAl intermetallic compound from solid oxides in molten CaCl2 and its corrosion behaviors in NaCl aqueous solution.Materials Chemistry and Physics,133(1),465-470. |
| MLA | H. Y. Yin,et al."Electrochemical preparation of NiAl intermetallic compound from solid oxides in molten CaCl2 and its corrosion behaviors in NaCl aqueous solution".Materials Chemistry and Physics 133.1(2012):465-470. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。