Preparation of SiC Fiber Reinforced Nickel Matrix Composite
文献类型：期刊论文
| 作者 | L. Zhang ; N. L. Shi ; J. Gong ; C. Sun |
| 刊名 | Journal of Materials Science & Technology
 |
| 出版日期 | 2012 |
| 卷号 | 28期号:3页码:234-240 |
| 关键词 | SiC fiber Composite Diffusion barrier layer Precursor wire metal-matrix theoretical-model microstructure fabrication |
| ISSN号 | 1005-0302 |
| 中文摘要 | A method of preparing continuous (Al+Al2O3)-coated SiC fiber reinforced nickel matrix composite was presented, in which the diffusion between SiC fiber and nickel matrix could be prevented. Magnetron sputtering is used to deposit Ni coating on the surface of the (Al+Al2O3)-coated SiC fiber in preparation of the precursor wires. It is shown that the deposited Ni coating combines well with the (Al+Al2O3) coating and has little negative effect on the tensile strength of (Al+Al2O3)-coated SiC fiber. Solid-state diffusion bonding process is employed to prepare the (Al+Al2O3)-coated SiC fiber reinforced nickel matrix with 37% fibers in volume. The solid-state diffusion bonding process is optimized and the optimum parameters are temperature of 870 degrees, pressure of 50 MPa and holding time of 2 h. Under this condition, the precursor wires can diffuse well, composite of full density can be formed and the (Al+Al2O3) coating is effective to restrict the reaction between SiC fiber and nickel matrix. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/60443]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. Zhang,N. L. Shi,J. Gong,et al. Preparation of SiC Fiber Reinforced Nickel Matrix Composite[J]. Journal of Materials Science & Technology,2012,28(3):234-240. |
| APA | L. Zhang,N. L. Shi,J. Gong,&C. Sun.(2012).Preparation of SiC Fiber Reinforced Nickel Matrix Composite.Journal of Materials Science & Technology,28(3),234-240. |
| MLA | L. Zhang,et al."Preparation of SiC Fiber Reinforced Nickel Matrix Composite".Journal of Materials Science & Technology 28.3(2012):234-240. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。