Rafting structure formation during solution treatment in a nickel-based superalloy
文献类型：期刊论文
| 作者 | K. Zhao ; L. H. Lou |
| 刊名 | International Journal of Materials Research
 |
| 出版日期 | 2012 |
| 卷号 | 103期号:3页码:309-312 |
| 关键词 | Superalloy Rafting Electron backscatter diffraction Stress high-volume fraction single-crystals internal-stresses high-temperature creep gamma phase diffraction morphology microstructure |
| ISSN号 | 1862-5282 |
| 中文摘要 | When solution treatment was carried out at 1 553 K, a rafting structure formed even above the dissolution temperature of the gamma' phase in a liquid metal cooling directionally solidified nickel-based superalloy. This abnormal coarsening behavior may be induced by the phase transformation stress due to the dissolution of non-uniform distribution of the gamma/gamma' eutectic. Electron backscatter diffraction and transmission electron microscopy were employed to analyze the stress. |
| 原文出处 | |
| 公开日期 | 2013-02-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/60482]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | K. Zhao,L. H. Lou. Rafting structure formation during solution treatment in a nickel-based superalloy[J]. International Journal of Materials Research,2012,103(3):309-312. |
| APA | K. Zhao,&L. H. Lou.(2012).Rafting structure formation during solution treatment in a nickel-based superalloy.International Journal of Materials Research,103(3),309-312. |
| MLA | K. Zhao,et al."Rafting structure formation during solution treatment in a nickel-based superalloy".International Journal of Materials Research 103.3(2012):309-312. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。