Low-temperature combustion synthesis of CuCr2O4 spinel powder for spectrally selective paints
文献类型:期刊论文
作者 | Geng QF(耿庆芬)2,3; Zhao X(赵鑫)1; Gao XH(高祥虎)1; Yang SR(杨生荣)2; Liu G(刘刚)1 |
刊名 | Journal of Sol-Gel Science and Technology |
出版日期 | 2012 |
卷号 | 61期号:1页码:281-288 |
ISSN号 | 0928-0707 |
关键词 | CuCr2O4 powder Sol-gel combustion Spectrally selective paint coatings Durability |
通讯作者 | 刘刚 |
英文摘要 | CuCr2O4 spinel powder with high quality black hue, investigated as solar-absorbing pigment for spectrally selective paint, was synthesized by an environmental friendly sol-gel combustion process using citric acid as the fuel and metal nitrates as oxidizers. Single-phase CuCr2O4 spinel crystals were obtained after heat treatment of the as burnt powder at a low temperature (600 C) and the average crystallite size of the CuCr2O4 powders increased with the calcining temperature. Morphological analysis of powders calcined at various temperatures was done by field emission scanning electron microscopy. CuCr2O4 powder calcined at 700 C was chosen as pigment to fabricate thickness sensitive spectrally selective paint coatings by simple spray-coating technique. For the sake of comparison, the as-burnt powder composed of mixed metal oxides (i.e., CuO and Cr2O3) was also used as pigment. The results reveal that the spinel CuCr2O4 based paint coatings exhibit much higher spectral selectivity (as = 0.88-0.91, e100 =0.27-0.35) which is depending on the coating thicknesses than that of coatings using as-burnt powder as pigment (as = 0.83-0.88, e100 = 0.60-0.66). The CuCr2O4-based paint coatings showed no visible degradation after 600 h of condensation test and the performance criterion value is 0.04, indicating that the coatings have excellent long term stability. |
学科主题 | 环境材料与生态化学 |
资助信息 | the ‘‘Western Light’’ Talents Training Program of CAS;the Solar Action Plan of CAS (Grant 1731012394) and National Natural Science Foundation of China (Grant 51003111) |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000299083700040 |
公开日期 | 2013-03-24 |
源URL | [http://210.77.64.217/handle/362003/2551] |
专题 | 兰州化学物理研究所_环境材料与生态化学研究发展中心 兰州化学物理研究所_固体润滑国家重点实验室 |
作者单位 | 1.Chinese Acad Sci, Lanzhou Inst Chem Phys, Res & Dev Ctr Ecomat & Ecochem, Lanzhou 730000, Peoples R China 2.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China 3.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Geng QF,Zhao X,Gao XH,et al. Low-temperature combustion synthesis of CuCr2O4 spinel powder for spectrally selective paints[J]. Journal of Sol-Gel Science and Technology,2012,61(1):281-288. |
APA | Geng QF,Zhao X,Gao XH,Yang SR,&Liu G.(2012).Low-temperature combustion synthesis of CuCr2O4 spinel powder for spectrally selective paints.Journal of Sol-Gel Science and Technology,61(1),281-288. |
MLA | Geng QF,et al."Low-temperature combustion synthesis of CuCr2O4 spinel powder for spectrally selective paints".Journal of Sol-Gel Science and Technology 61.1(2012):281-288. |
入库方式: OAI收割
来源:兰州化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。