Growth and spectral characteristics of Yb3+-doped LiLa(MoO4)(2) crystal
文献类型：期刊论文
| 作者 | X. Y. Huang ; Z. B. Lin ; L. Z. Zhang ; G. F. Wang |
| 刊名 | Journal of Crystal Growth
 |
| 出版日期 | 2007-08 |
| 卷号 | 306期号:1页码:208-211 |
| 关键词 | optical microscopy growth from melt molybdate solid state laser materials laser operation average power kyb(wo4)(2) absorption |
| ISSN号 | 0022-0248 |
| 中文摘要 | A Yb3+-doped LiLa(MoO4)(2) crystal with dimension of phi 20 x 35 mm(3) has been grown by the Czochralski method. The polarized optical absorption and emission spectra of the crystal have been investigated. The Yb3+ :LiLa(MoO4)(2) crystal has a broad absorption FWHM of 29 mn at 977 nm. The absorption cross-sections of the crystals are 1.93 x 10(-20) Cm-2 and 1.56 x 10(-20) Cm-2 at 977 nm for pi- and sigma-polarization, respectively. The emission cross-sections of the crystals are 1.53 x 10(-20) and 1.00 X 10(-20)Cm(2) at 1011 nm for pi- and sigma-polarization, respectively. The radiative lifetime and fluorescence lifetime of the Yb 3+ :LiLa(MO04)2 crystal are 391 and 636ps, respectively. The laser performance parameters beta(min), I-past, and I-min of the crystal have been calculated. The investigated results shown the Yb3+ :LiLa(MOO4)(2) crystal is expected as a potential solid-state laser crystal materials. (c) 2007 Elsevier B.V. All rights reserved. |
| 语种 | 英语 |
| 公开日期 | 2013-04-01 |
| 源URL | [http://ir.fjirsm.ac.cn/handle/350002/6329]  |
| 专题 | 福建物质结构研究所_中科院福建物质结构研究所_期刊论文 |
| 推荐引用方式 GB/T 7714 | X. Y. Huang,Z. B. Lin,L. Z. Zhang,et al. Growth and spectral characteristics of Yb3+-doped LiLa(MoO4)(2) crystal[J]. Journal of Crystal Growth,2007,306(1):208-211. |
| APA | X. Y. Huang,Z. B. Lin,L. Z. Zhang,&G. F. Wang.(2007).Growth and spectral characteristics of Yb3+-doped LiLa(MoO4)(2) crystal.Journal of Crystal Growth,306(1),208-211. |
| MLA | X. Y. Huang,et al."Growth and spectral characteristics of Yb3+-doped LiLa(MoO4)(2) crystal".Journal of Crystal Growth 306.1(2007):208-211. |