Effect of End Groups on Optoelectronic Properties of Poly(9,9-dioctylfluorene): A Study with Hexadecylfluorenes as Model Polymers
文献类型：期刊论文
| 作者 | Wang QL ; Zhang BH ; Liu LH ; Chen YG ; Qu Y ; Zhang XJ ; Yang JW ; Xie ZY ; Geng YH ; Wang LX ; Wang FS |
| 刊名 | journal of physical chemistry c
 |
| 出版日期 | 2012 |
| 卷号 | 116期号:41页码:21727-21733 |
| 关键词 | LIGHT-EMITTING-DIODES ORGANIC SOLAR-CELLS CONJUGATED POLYMERS MOLECULAR-WEIGHT HOLE TRANSPORT GREEN EMISSION POLYFLUORENE EFFICIENCY DEFECTS BLUE |
| ISSN号 | 1932-7447 |
| 通讯作者 | xie zy |
| 中文摘要 | monodisperse hexadecyl(9,9-dioctylfluorene)s f16, brf16, and bf16, which comprise h, br, and boronic pinacol ester end groups, respectively, were synthesized, and the effect of these end groups on the photophysical, electrochemical, and electroluminescent properties of the polymers were investigated. the end groups have no noticeable effect on the energy levels of the polymers. f16 and brf16 show high photoluminescence (pl) quantum yields (phi s) in both solution and film states. film pl phi s (phi(film)s) of f16 and brf16 are 0.72 and 0.79, respectively. these values are about 1.4-1.5 times of that of bf16 and poly(9,9-dioctylfluorene) (pfo) prepared by suzuki polycondensation. moreover, phi(film)s of f16 and brf16 were kept almost the same after thermal annealing at 120 degrees c in both air and argon atmospheres. by contrast, the phi(film)s of bf16 and pfo dramatically decreased to 0.25 and 0.2.9 after thermal annealing at 120 degrees c in air. polymer light-emitting diodes (pleds) were fabricated. f16, brf16, and pfo exhibited maximum luminance efficiencies of 0.60, 0.27, and 0.39 cd.a(-1), respectively; while that of bf16 was as low as 0.024 cd.a(-1). meanwhile, green emission was observed for devices of brf16, bf16, and pfo, but not for devices of f16. electron- and hole-only devices were fabricated for elucidating the effect of end groups on charge transporting properties of the polymers. while br is a mild hole-trapper, boronic ester group traps both holes and electrons, resulting in severely unbalanced hole- and electron-transport. our results indicate that boronic ester end groups have a detrimental effect on the optoelectronic properties of polyfluorenes larger than br. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000309902100011 |
| 公开日期 | 2013-04-22 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/47892]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Wang QL,Zhang BH,Liu LH,et al. Effect of End Groups on Optoelectronic Properties of Poly(9,9-dioctylfluorene): A Study with Hexadecylfluorenes as Model Polymers[J]. journal of physical chemistry c,2012,116(41):21727-21733. |
| APA | Wang QL.,Zhang BH.,Liu LH.,Chen YG.,Qu Y.,...&Wang FS.(2012).Effect of End Groups on Optoelectronic Properties of Poly(9,9-dioctylfluorene): A Study with Hexadecylfluorenes as Model Polymers.journal of physical chemistry c,116(41),21727-21733. |
| MLA | Wang QL,et al."Effect of End Groups on Optoelectronic Properties of Poly(9,9-dioctylfluorene): A Study with Hexadecylfluorenes as Model Polymers".journal of physical chemistry c 116.41(2012):21727-21733. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。