Microstructure, oxidation protection and failure mechanism of Yb2SiO5/LaMgAl11O19 coating deposited on C/SiC composites by atmospheric plasma spraying
文献类型：期刊论文
| 作者 | Zou BL ; Khan ZS ; Gu LJ ; Fan XZ ; Huang WZ ; Wang Y ; Zhao Y ; Wang CJ ; Yang KY ; Ma HM ; Cao XQ |
| 刊名 | corrosion science
 |
| 出版日期 | 2012 |
| 卷号 | 62页码:192-200 |
| 关键词 | C/C-SIC COMPOSITES COATED CARBON/CARBON COMPOSITES SILICON-CARBIDE COMPOSITES THERMAL BARRIER COATINGS YTTRIUM SILICATE BEHAVIOR HEXAALUMINATE TEMPERATURE MO |
| ISSN号 | 0010-938x |
| 通讯作者 | cao xq |
| 中文摘要 | c/sic composites were plasma sprayed with an yb2sio5/lamgal11o19 coating to improve the oxidation resistance. microstructure, oxidation protection and failure mechanism of the coating during dynamic thermal cycling (dtc) were investigated. the results showed that good interfacial bonding between the substrate and coating was present before and after dtc. weight loss for the sample coated on one-side was 4.1% after 11 cycles of heating for 85 min, for the uncoated sample it was as high as 20.6%. failure mechanism of the coating resulted from the reaction sintering of the coating and the formation of bubbles between the substrate and the coating. (c) 2012 elsevier ltd. all rights reserved. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000307418000022 |
| 公开日期 | 2013-04-23 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/47979]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Zou BL,Khan ZS,Gu LJ,et al. Microstructure, oxidation protection and failure mechanism of Yb2SiO5/LaMgAl11O19 coating deposited on C/SiC composites by atmospheric plasma spraying[J]. corrosion science,2012,62:192-200. |
| APA | Zou BL.,Khan ZS.,Gu LJ.,Fan XZ.,Huang WZ.,...&Cao XQ.(2012).Microstructure, oxidation protection and failure mechanism of Yb2SiO5/LaMgAl11O19 coating deposited on C/SiC composites by atmospheric plasma spraying.corrosion science,62,192-200. |
| MLA | Zou BL,et al."Microstructure, oxidation protection and failure mechanism of Yb2SiO5/LaMgAl11O19 coating deposited on C/SiC composites by atmospheric plasma spraying".corrosion science 62(2012):192-200. |