An Optical Microscopy Study on the Phase Structure of Poly(L-lactide acid)/Poly(propylene carbonate) Blends
文献类型：期刊论文
| 作者 | Gao M ; Ren ZJ ; Yan SK ; Sun JR ; Chen XS |
| 刊名 | journal of physical chemistry b
 |
| 出版日期 | 2012 |
| 卷号 | 116期号:32页码:9832-9837 |
| 关键词 | INFRARED CORRELATION SPECTROSCOPY POLY(LACTIC ACID) POLY(VINYLIDENE FLUORIDE) POLY(BUTYLENE SUCCINATE) MELTING BEHAVIOR POLYMERIC BLENDS MORPHOLOGY CRYSTALLIZATION COMPOSITES TRANSITION |
| ISSN号 | 1520-6106 |
| 通讯作者 | yan sk |
| 中文摘要 | the dependence of phase structure of plla/ppc blends on the blend ratio, the heat-treatment temperature and time was investigated by optical microscopy. it is found that, at lower ppc content, e.g., less than 30%, the plla crystalline spherulites fill the whole space with the ppc dispersed in the amorphous region of plla. no evident phase separation has been observed under optical microscope. when the content of ppc reaches 40%, phase separation takes place. the phase separation of the plla/ppc blend happens prior to the crystallization of plla. therefore, the heat-treatment temperature and time are the two most important factors that control the phase structure of the blend. at low heat-treatment temperatures, e.g., lower than 190 degrees c, the ppc and the amorphous plla part compose a continuous phase with the crystalline plla domains dispersed in it. when the sample was heat-treated at 200 degrees c for s min, a bicontinuous phase structure was observed. with further increase of the heat-treatment temperature, the crystalline plla composes the continuous phase with ppc domains randomly dispersed in it. similar phase reversal phenomenon has also been observed by heat-treating the samples at 200 degrees c for different times. it is further confirmed that the crystallization of plla in the blends is influenced by the different phase structures. for example, the crystallinity of plla in the blend increases with increasing heat-treatment temperature. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000307494500030 |
| 公开日期 | 2013-04-23 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/47998]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Gao M,Ren ZJ,Yan SK,et al. An Optical Microscopy Study on the Phase Structure of Poly(L-lactide acid)/Poly(propylene carbonate) Blends[J]. journal of physical chemistry b,2012,116(32):9832-9837. |
| APA | Gao M,Ren ZJ,Yan SK,Sun JR,&Chen XS.(2012).An Optical Microscopy Study on the Phase Structure of Poly(L-lactide acid)/Poly(propylene carbonate) Blends.journal of physical chemistry b,116(32),9832-9837. |
| MLA | Gao M,et al."An Optical Microscopy Study on the Phase Structure of Poly(L-lactide acid)/Poly(propylene carbonate) Blends".journal of physical chemistry b 116.32(2012):9832-9837. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。