K3B6O10Br非线性光学晶体的生长及性质研究
文献类型：期刊论文
| 作者 | 张敏 ; 潘世烈; 王颖; 杨云; 张方方
|
| 刊名 | 人工晶体学报
 |
| 出版日期 | 2012 |
| 卷号 | 41期号:增刊页码:171-174 |
| 关键词 | K3B6O10Br 非线性光学晶体 晶体生长 光学性质 |
| ISSN号 | 1000-985X |
| 中文摘要 | 采用顶部籽晶法,KF.2H2O-PbO复合助熔剂生长K3B6O10Br晶体,获得了18 mm×18 mm×10 mm尺寸的单晶。K3B6O10Br紫外透过截止边约为210 nm,粉末倍频效应为3倍KDP,利用德拜公式计算了阴离子基团的偶极矩。采用直角棱镜法测试了晶体折射率并拟合了Sellmeier方程。计算及实验表明,K3B6O10Br能够实现532 nm及355 nm倍频输出。对晶体的激光损伤阈值、硬度及潮解性进行了测试。 |
| 英文摘要 | High quality K3B6O10Br single crystal with size up to 18 mm × 18 mm × 10 mm was obtained via top-seeded solution growth ( TSSG) method using KF·2H2O-PbO binary fluxes． The experiments show that the UV transmission cut off of K3B6O10 Br is about 210 nm． Nonlinear optical measurements demonstrate that the material has second harmonic generation ( SHG) properties，with efficiency approximately three times that of KH2PO4 ． The refractive index was test and fit the Sellmeier equation． SHG experiment indicates that the K3B6O10 Br can achieve 532 nm and 355 nm frequency-doubled wavelength． The damage threshold，hardness and deliquescence were reported． |
| 收录类别 | EI |
| 公开日期 | 2013-05-16 |
| 源URL | [http://ir.xjipc.cas.cn/handle/365002/2433]  |
| 专题 | 新疆理化技术研究所_新疆维吾尔自治区电子信息材料与器件重点实验室 新疆理化技术研究所_材料物理与化学研究室 |
| 作者单位 | 中国科学院新疆理化技术研究所;新疆电子信息材料与器件重点实验室；中科院研究生院 |
| 推荐引用方式 GB/T 7714 | 张敏,潘世烈,王颖,等. K3B6O10Br非线性光学晶体的生长及性质研究[J]. 人工晶体学报,2012,41(增刊):171-174. |
| APA | 张敏,潘世烈,王颖,杨云,&张方方.(2012).K3B6O10Br非线性光学晶体的生长及性质研究.人工晶体学报,41(增刊),171-174. |
| MLA | 张敏,et al."K3B6O10Br非线性光学晶体的生长及性质研究".人工晶体学报 41.增刊(2012):171-174. |
入库方式： OAI收割
来源：新疆理化技术研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。