Uniform Eu3+-doped YF3 microcrystals: inorganic salt-controlled synthesis and their luminescent properties
文献类型：期刊论文
| 作者 | Fu ZL ; Cui XY ; Cui SB ; Qi XD ; Zhou SH ; Zhang SY ; Jeong JH |
| 刊名 | crystengcomm
 |
| 出版日期 | 2012 |
| 卷号 | 14期号:11页码:3915-3922 |
| 关键词 | SHAPE-CONTROLLED SYNTHESIS EARTH FLUORIDE NANOCRYSTALS YBO3-EU NANOCRYSTALS SILVER NANOPARTICLES POLYOL SYNTHESIS SINGLE-CRYSTAL SIZE COLLOIDS GLASS IONS |
| ISSN号 | 1466-8033 |
| 通讯作者 | fu zl |
| 中文摘要 | a variety of microstructured yf3:eu3+ with different morphologies have been successfully synthesized using a simple inorganic salt as the only structure-directing agent in the hydrothermal system. the cations of al3+, li+, mg2+, na+, k+ and ba2+ were found to determine the size and morphology of the as-prepared microstructured yf3. the prepared samples were systematically characterized by powder x-ray diffraction (xrd), field emission-scanning electron microscopy (fe-sem), transmission electron microscopy (tem), photoluminescence (pl) and photoluminescent excitation spectra (ple). detailed proofs indicated that the process of growing different morphologies of yf3:eu3+ microparticles were dominated by different growth mechanisms. furthermore, photoluminescent properties were also investigated. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000304059800015 |
| 公开日期 | 2013-06-30 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/48567]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Fu ZL,Cui XY,Cui SB,et al. Uniform Eu3+-doped YF3 microcrystals: inorganic salt-controlled synthesis and their luminescent properties[J]. crystengcomm,2012,14(11):3915-3922. |
| APA | Fu ZL.,Cui XY.,Cui SB.,Qi XD.,Zhou SH.,...&Jeong JH.(2012).Uniform Eu3+-doped YF3 microcrystals: inorganic salt-controlled synthesis and their luminescent properties.crystengcomm,14(11),3915-3922. |
| MLA | Fu ZL,et al."Uniform Eu3+-doped YF3 microcrystals: inorganic salt-controlled synthesis and their luminescent properties".crystengcomm 14.11(2012):3915-3922. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。