Synthesis and structural analysis of a regular Cu-Mg-Alhydrotalcite-like compound

文献类型:期刊论文

作者Wu, Jian-Song ; Liu, Yu-Ping ; Liang, Mei-Fang ; Cheng, Jian ; Wan, Jian-Ping ; Chen, Ling-Zhu
刊名TURKISH JOURNAL OF CHEMISTRY
出版日期2011
卷号35期号:6页码:881-891
关键词Glycol hydrothermal Cu-Mg-Al hydrotalcite-like compound synthesis
英文摘要A fine-quality, regular Cu-Mg-Al hydrotalcite-like compound was synthesized via the glycothermal method using CuCl(2)center dot 2H(2)O, MgCl(2)center dot 6H(2)O, AlCl(3)center dot 6H(2)O, and Na(2)CO(3) as raw materials and sodium hydroxide as the precipitant. Hydrotalcite samples were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy, thermogravimetric-differential thermal analysis, and Brunauer-Emmett-Teller N(2) surface area measurements. The influence of glycol content on the characteristics of the sample was investigated. The results show that the glycol content in the system had a greater impact on regular hydrotalcite with an intercalated structure. A Cu-Mg-Al hydrotalcite-like compound with a well-defined shape, distinct intercalated structure, regular quality, and good dispersing capability could be obtained under the following conditions: glycol volume ratio of 10%, hydrothermal temperature of 180 degrees C, and reaction time of 15 h. The compound obtained was well crystallized and had the morphology of a homogeneous and hexagonal sheet. The thickness of each hexagon in the hydrotalcite was about 40 nm, which was consistent with the value estimated with the Scherer equation. A fine-quality, regular Cu-Mg-Al hydrotalcite-like compound was synthesized via the glycothermal method using CuCl(2)center dot 2H(2)O, MgCl(2)center dot 6H(2)O, AlCl(3)center dot 6H(2)O, and Na(2)CO(3) as raw materials and sodium hydroxide as the precipitant. Hydrotalcite samples were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy, thermogravimetric-differential thermal analysis, and Brunauer-Emmett-Teller N(2) surface area measurements. The influence of glycol content on the characteristics of the sample was investigated. The results show that the glycol content in the system had a greater impact on regular hydrotalcite with an intercalated structure. A Cu-Mg-Al hydrotalcite-like compound with a well-defined shape, distinct intercalated structure, regular quality, and good dispersing capability could be obtained under the following conditions: glycol volume ratio of 10%, hydrothermal temperature of 180 degrees C, and reaction time of 15 h. The compound obtained was well crystallized and had the morphology of a homogeneous and hexagonal sheet. The thickness of each hexagon in the hydrotalcite was about 40 nm, which was consistent with the value estimated with the Scherer equation.
收录类别SCI
语种英语
公开日期2013-08-22
源URL[http://ir.isl.ac.cn/handle/363002/1894]  
专题青海盐湖研究所_青海盐湖研究所知识仓储
中国科学院青海盐湖研究所
推荐引用方式
GB/T 7714
Wu, Jian-Song,Liu, Yu-Ping,Liang, Mei-Fang,et al. Synthesis and structural analysis of a regular Cu-Mg-Alhydrotalcite-like compound[J]. TURKISH JOURNAL OF CHEMISTRY,2011,35(6):881-891.
APA Wu, Jian-Song,Liu, Yu-Ping,Liang, Mei-Fang,Cheng, Jian,Wan, Jian-Ping,&Chen, Ling-Zhu.(2011).Synthesis and structural analysis of a regular Cu-Mg-Alhydrotalcite-like compound.TURKISH JOURNAL OF CHEMISTRY,35(6),881-891.
MLA Wu, Jian-Song,et al."Synthesis and structural analysis of a regular Cu-Mg-Alhydrotalcite-like compound".TURKISH JOURNAL OF CHEMISTRY 35.6(2011):881-891.

入库方式: OAI收割

来源:青海盐湖研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。