hydrogenstoragecapacityofnickelsupportedonametalorganicframeworkcompoundundermildconditions
文献类型：期刊论文
| 作者 | Liu YY(刘颖雅); Zhang J(张箭); Ceng JL(曾巨澜); Chu HL(褚海亮); Xu F(徐芬); Sun LX(孙立贤) |
| 刊名 | chinesejournalofcatalysis
 |
| 出版日期 | 2008-01-01 |
| 卷号 | 29期号:7页码:655 |
| ISSN号 | 0253-9837 |
| 英文摘要 | The traditional impregnation method was used to support nickel ions on the metal-organic framework compound MIL-101 (Cr3F(H2O)(2)O(O2C)-C6H4-(CO2)(3)center dot nH(2)O, n approximate to 5) for the preparation of a Ni/MIL-101 composite material. With two ways of impregnation (excessive impregnation and incipient wetness impregnation) followed by two ways of reduction (liquid chemical reduction and solid hydrogenation reduction), four Ni/MIL-101 samples were obtained. The hydrogen storage capacity of the Ni/MIL-101 samples was measured under mild conditions (25-100 degrees C, 0.01-4 MPa). Compared with the original MIL-101, Ni/MIL-101 had high hydrogen storage capacity because of the Ni particles supported on MIL-101. Among these samples, the sample prepared by excessive impregnation followed by liquid chemical reduction exhibited the highest hydrogen storage capacity of 1.02% at 100 degrees C and 4.0 MPa. |
| 语种 | 英语 |
| 源URL | [http://cas-ir.dicp.ac.cn/handle/321008/174546]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 中国科学院大连化学物理研究所 |
| 推荐引用方式 GB/T 7714 | Liu YY,Zhang J,Ceng JL,et al. hydrogenstoragecapacityofnickelsupportedonametalorganicframeworkcompoundundermildconditions[J]. chinesejournalofcatalysis,2008,29(7):655. |
| APA | 刘颖雅,张箭,曾巨澜,褚海亮,徐芬,&孙立贤.(2008).hydrogenstoragecapacityofnickelsupportedonametalorganicframeworkcompoundundermildconditions.chinesejournalofcatalysis,29(7),655. |
| MLA | 刘颖雅,et al."hydrogenstoragecapacityofnickelsupportedonametalorganicframeworkcompoundundermildconditions".chinesejournalofcatalysis 29.7(2008):655. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。