Studies on high performance nonvolatile polyimides coating: Gamma ray initiated bulk copolymerization of vinyl polar monomer and maleimide-terminated polyimides with flexible backbone and the modifications
文献类型：期刊论文
| 作者 | Qi HX ; Liu F ; Zhang N ; Chen YW ; Yang HL ; Wang Z |
| 刊名 | progress in organic coatings
 |
| 出版日期 | 2012 |
| 卷号 | 73期号:1页码:33-41 |
| 关键词 | THERMOPLASTIC-TOUGHENED THERMOSETS POLYMERIZATION ANHYDRIDE RESINS EPOXY DIANHYDRIDE RADIATION |
| ISSN号 | 0300-9440 |
| 通讯作者 | liu f |
| 中文摘要 | the objective of the present work was to develop a nonvolatile coating involving vinyl polar monomer and high performance maleimide-terminated polyimides (mtps) with flexible backbone. the synthesized mtps with different molecular weight (mw) showed good solubility in n-vinylpyrroliclone (nvp), and the homogeneous binary systems were obtained even when the content of mtfs reached 50 wt%. nvp-mtps copolymer resin were prepared by gamma ray initiated bulk copolymerization, followed by thermal postcuring to improve the properties. nvp-mtps copolymer resins exhibited flexural strength higher than 76 mpa, glass transition (t(g)) higher than 142 degrees c, thermal stability (t(5%)) no less than 214 degrees c, but relatively poor impact strength and water resistance property. it was revealed that increasing mw of mtps would result in the increase of impact strength and a decrease of thermal and flexural properties of copolymer resin, accompanied with the gradual decrease of gel percentage of copolymer resin. amino-terminated linear polyimide (atlp) was introduced to modify nvp-mtps copolymer resin and the c-n linkage was formed from terminal nh(2) to electron deficient double bone on maleimide ring of mtps via michael nucleophilic addition. polyvinylsiloxane (pvs) were introduced to modify nvp-mtps copolymer resin by in situ ring opening polymerization followed with copolymerization under gamma ray initiation. the introduction of both modifiers led to an appreciable increase of impact strength and a remarkable water uptake decrease, meanwhile, other properties including thermal and flexural properties of modified copolymer resins maintained and even exhibited a slight increase. fracture surface morphology by scanning electron microscopy (sem) technique showed that introduction of both modifiers maintained good homogeneity of copolymer resin, and led to a gradual transition from rigid deformation to plastic deformation. (c) 2011 elsevier b.v. all rights reserved. |
| 收录类别 | SCI收录期刊论文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000298072200006 |
| 公开日期 | 2013-09-03 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/48775]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Qi HX,Liu F,Zhang N,et al. Studies on high performance nonvolatile polyimides coating: Gamma ray initiated bulk copolymerization of vinyl polar monomer and maleimide-terminated polyimides with flexible backbone and the modifications[J]. progress in organic coatings,2012,73(1):33-41. |
| APA | Qi HX,Liu F,Zhang N,Chen YW,Yang HL,&Wang Z.(2012).Studies on high performance nonvolatile polyimides coating: Gamma ray initiated bulk copolymerization of vinyl polar monomer and maleimide-terminated polyimides with flexible backbone and the modifications.progress in organic coatings,73(1),33-41. |
| MLA | Qi HX,et al."Studies on high performance nonvolatile polyimides coating: Gamma ray initiated bulk copolymerization of vinyl polar monomer and maleimide-terminated polyimides with flexible backbone and the modifications".progress in organic coatings 73.1(2012):33-41. |