Testing Atmosphere Effect on Friction and Wear Behaviors of Duplex TiC/a-C(Al) Nanocomposite Carbon-Based Coating

文献类型:期刊论文

作者Zhou SG(周升国)1,2; Wang LP(王立平)1; Xue QJ(薛群基)1
刊名Tribology Letters
出版日期2012
卷号47期号:3页码:435-446
关键词nc-TiC/a-C(Al) Nanocomposite Atmosphere Tribo-layer
ISSN号1023-8883
通讯作者王立平
英文摘要Due to strongly tribological atmosphere sensitivity of carbon-based coatings, it is of extreme significance to investigate their friction and wear behaviors in different atmospheres. In this letter, duplex nc-TiC/a-C(Al) nanocomposite carbon-based coating coupled with high hardness, low internal stress and high adhesion strength was successfully fabricated using magnetron sputtering process. The friction and wear behaviors of as-fabricated coating were evaluated in dry N2, humid N2, air, dry O2, and humid O2 atmospheres, respectively. Results show that the as-fabricated coating possesses very high friction and wear due to the strong covalent bond interactions at the sliding interface caused by the free σ-bonds on the coating surface in dry N2 atmosphere. Whereas the free σ-bonds can be efficiently terminated and passivated by water and/or oxygen molecules to weaken the strong covalent bond interactions to result in low friction and wear of coating in humid N2, air, dry O2, and humid O2 atmospheres. The compact and homogeneous carbonaceous tribo-layer on the counterpart is mainly responsible for the lowest friction and wear of coating in humid N2 atmosphere. Whereas the tribo-layer can be restrained to a certain extent by the tribo-chemical reaction, especially it results in a nearly negligible carbonaceous tribo-layer on the counterpart in dry O2 atmosphere, which is mainly responsible for largely increased friction and wear of coating.
学科主题材料科学与物理化学
收录类别SCI
资助信息the National Natural Science Foundation of China (Grant Nos. 50905178 & 11172300)
语种英语
WOS记录号WOS:000307295100012
公开日期2013-07-12
源URL[http://210.77.64.217/handle/362003/3497]  
专题兰州化学物理研究所_固体润滑国家重点实验室
作者单位1.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China
2.Jiangxi Univ Sci & Technol, Sch Mat Sci & Engn, Ganzhou 341000, Jiangxi, Peoples R China
推荐引用方式
GB/T 7714
Zhou SG,Wang LP,Xue QJ. Testing Atmosphere Effect on Friction and Wear Behaviors of Duplex TiC/a-C(Al) Nanocomposite Carbon-Based Coating[J]. Tribology Letters,2012,47(3):435-446.
APA Zhou SG,Wang LP,&Xue QJ.(2012).Testing Atmosphere Effect on Friction and Wear Behaviors of Duplex TiC/a-C(Al) Nanocomposite Carbon-Based Coating.Tribology Letters,47(3),435-446.
MLA Zhou SG,et al."Testing Atmosphere Effect on Friction and Wear Behaviors of Duplex TiC/a-C(Al) Nanocomposite Carbon-Based Coating".Tribology Letters 47.3(2012):435-446.

入库方式: OAI收割

来源:兰州化学物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。