The Tribological Behaviour of Fe-28Al-5Cr/TiC Under Liquid Paraffine Lubrication
文献类型：期刊论文
| 作者 | Zhang XH(张兴华)1,2 ; Yang J(杨军)1; Ma JQ(马吉强)1; Hao JY(郝俊英)1; Bi QL(毕秦岭)1; Liang YM(梁永民)1; Liu WM(刘维民)1
|
| 刊名 | Tribology Letters
 |
| 出版日期 | 2012 |
| 卷号 | 45期号:1页码:109-116 |
| 关键词 | Fe(3)Al Intermetallics Fe(3)Al-TiC composites Oil lubrication Wear mechanism |
| ISSN号 | 1023-8883 |
| 通讯作者 | 杨军 |
| 英文摘要 | The tribological behaviour of Fe-28Al-5Cr and its composites containing 15, 25 and 50 wt% TiC (corresponding to 19.3, 31.2 and 57.6 vol%), produced by hot-pressing process, was investigated under liquid paraffine lubrication against an AISI 52100 steel ball in ambient environment at varied applied loads and sliding speeds. It was found that the wear resistance increased and friction coefficient decreased with increasing of TiC content. The coefficients of friction are in the range of 0.09-0.14 at the given testing conditions. The wear rates of all the materials except the 50% composite are on the order of 10-6-10-5 mm3 m-1, the wear rate for the 50% composite is too low to quantify under the two sliding conditions, (50 N, 0.04 m/s) and (100 N, 0.02 m/s). The wear rates of all the materials increase as applied load increases and the increasing extent diminishes with the increase of TiC content, but first increase slightly and then nearly remains steadiness with increasing sliding speed. The 50 wt% composite has wear resistance about 7-20 times better than pure Fe-28Al-5Cr at different sliding parameters. The enhanced wear resistance by TiC addition is attributed to the high hardness of the composites, as well as support of the oil lubrication film/layer by the hard TiC phase. The worn surfaces of all the materials are analyzed by a scanning electron microscope. The dominant wear mechanism of the Fe-28Al-5Cr and 15% composite is grooving and flaking-off, but those of the 25 and 50% composites are mainly shallow grooving. |
| 学科主题 | 材料科学与物理化学 |
| 收录类别 | SCI |
| 资助信息 | the National Natural Science Foundation of China (50801064;50905177);the National 973 Project of China (2007CB607601) |
| 语种 | 英语 |
| WOS记录号 | WOS:000298646700010 |
| 公开日期 | 2013-07-12 |
| 源URL | [http://210.77.64.217/handle/362003/3507]  |
| 专题 | 兰州化学物理研究所_固体润滑国家重点实验室 |
| 作者单位 | 1.Chinese Acad Sci, State Key Lab Solid Lubricat, Lanzhou Inst Chem Phys, Lanzhou 730000, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100039, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang XH,Yang J,Ma JQ,et al. The Tribological Behaviour of Fe-28Al-5Cr/TiC Under Liquid Paraffine Lubrication[J]. Tribology Letters,2012,45(1):109-116. |
| APA | Zhang XH.,Yang J.,Ma JQ.,Hao JY.,Bi QL.,...&Liu WM.(2012).The Tribological Behaviour of Fe-28Al-5Cr/TiC Under Liquid Paraffine Lubrication.Tribology Letters,45(1),109-116. |
| MLA | Zhang XH,et al."The Tribological Behaviour of Fe-28Al-5Cr/TiC Under Liquid Paraffine Lubrication".Tribology Letters 45.1(2012):109-116. |
入库方式： OAI收割
来源：兰州化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。