Low-temperature prepared highly effective ferric hydroxide supported gold catalysts for carbon monoxide selective oxidation in the presence of hydrogen
文献类型：期刊论文
| 作者 | Deng YQ(邓友全) ; Deng YQ(邓友全)
|
| 刊名 | Applied Catalysis A: General
 |
| 出版日期 | 2008 |
| 卷号 | 340页码:220-228 |
| 关键词 | Gold catalyst CO selective oxidation Preparation Uncalcined Low-temperature |
| ISSN号 | 0926-860X |
| 通讯作者 | 邓友全 |
| 中文摘要 | Ferric hydroxide supported Au catalysts prepared with co-precipitation method at room temperature without any heat treatment hereafter exhibited high catalytic activity and selectivity for CO oxidation in air and CO selective oxidation in the presence of H2. With calcination temperature rising, both activity and selectivity decreased. X-ray Photoelectron Spectra (XPS) indicated that Au existed as Au0 and Au+ in the catalyst without heat treatment and even after being calcined at 200 ℃, while after being calcined at 400 ℃, Au existed as Au0 completely. X-ray Diffraction (XRD) and High Resolution Transmission Electron Microscopic (HRTEM) investigations indicated that both the supports and Au species were highly dispersed as nano or sub-nano particles even after being calcined at 200 ℃, but after being calcined at 400 ℃ the supports transformed to crystal Fe2O3 with typical diameter of 30 nm and Au species aggregated to nano-particles with typical diameter of 2–4 nm. HRTEM investigations also suggested that the supports calcined at 200 ℃ were composed of amorphous ferric hydroxide and crystal ferric oxide. Results of computer simulation (CS) showed that O2 was adsorbed on Au crystal cell and then were activated, which should be the key factor for the subsequent reaction. It also suggested that O2 species were more easily adsorbed on Au+ than on Au0, indicating that higher positive charge of the Au species possessed the higher activity for CO oxidation. |
| 学科主题 | 物理化学 |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000256327600010 |
| 公开日期 | 2013-08-19 |
| 源URL | [http://210.77.64.217/handle/362003/3644]  |
| 专题 | 兰州化学物理研究所_绿色化学研究发展中心 |
| 通讯作者 | Deng YQ(邓友全); Deng YQ(邓友全) |
| 推荐引用方式 GB/T 7714 | Deng YQ,Deng YQ. Low-temperature prepared highly effective ferric hydroxide supported gold catalysts for carbon monoxide selective oxidation in the presence of hydrogen[J]. Applied Catalysis A: General,2008,340:220-228. |
| APA | 邓友全,&邓友全.(2008).Low-temperature prepared highly effective ferric hydroxide supported gold catalysts for carbon monoxide selective oxidation in the presence of hydrogen.Applied Catalysis A: General,340,220-228. |
| MLA | 邓友全,et al."Low-temperature prepared highly effective ferric hydroxide supported gold catalysts for carbon monoxide selective oxidation in the presence of hydrogen".Applied Catalysis A: General 340(2008):220-228. |
入库方式： OAI收割
来源：兰州化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。