Comparative Study of Stress Corrosion Cracking Behaviors of Typical Microstructures of Weld Heat-Affected Zones of E690 High-Strength Low-Alloy Steel in SO2-Containing Marine Environment
文献类型：期刊论文
| 作者 | Ma Hongchi; Du Cuiwei; Liu Zhiyong; Li Yong; Li Xiaogang |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2019 |
| 卷号 | 55期号:4页码:469-479 |
| 关键词 | ATMOSPHERIC CORROSION |
| DOI | 10.11900/0412.1961.2018.00140 |
| 英文摘要 | Comparative Study of Stress Corrosion Cracking Behaviors of Typical Microstructures of Weld Heat-Affected Zones of E690 High-Strength Low-Alloy Steel in SO2-Containing Marine Environment |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/18391]  |
| 专题 | 2019专题 |
| 作者单位 | Liu, ZY (reprint author), Univ Sci & Technol Beijing, Key Lab Corros & Protect MOE, Corros & Protect Ctr, Beijing 100083, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Ma Hongchi,Du Cuiwei,Liu Zhiyong,et al. Comparative Study of Stress Corrosion Cracking Behaviors of Typical Microstructures of Weld Heat-Affected Zones of E690 High-Strength Low-Alloy Steel in SO2-Containing Marine Environment[J]. ACTA METALLURGICA SINICA,2019,55(4):469-479. |
| APA | Ma Hongchi,Du Cuiwei,Liu Zhiyong,Li Yong,&Li Xiaogang.(2019).Comparative Study of Stress Corrosion Cracking Behaviors of Typical Microstructures of Weld Heat-Affected Zones of E690 High-Strength Low-Alloy Steel in SO2-Containing Marine Environment.ACTA METALLURGICA SINICA,55(4),469-479. |
| MLA | Ma Hongchi,et al."Comparative Study of Stress Corrosion Cracking Behaviors of Typical Microstructures of Weld Heat-Affected Zones of E690 High-Strength Low-Alloy Steel in SO2-Containing Marine Environment".ACTA METALLURGICA SINICA 55.4(2019):469-479. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。