Effects of alloying elements on the corrosion behavior of Ni-based alloys in molten NaCl-KCl-MgCl(2 )salt at different temperatures
文献类型：期刊论文
| 作者 | Sun, H; Zhang, P; Wang, JQ |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2018 |
| 卷号 | 143期号:-页码:187-199 |
| ISSN号 | 0010-938X |
| 关键词 | THERMAL-ENERGY STORAGE CONCENTRATING SOLAR POWER SALT NICKEL COMPATIBILITY LICL ATMOSPHERES MECHANISMS RESISTANCE CHROMIUM |
| DOI | 10.1016/j.corsci.2018.08.021 |
| 文献子类 | 期刊论文 |
| 英文摘要 | The effects of alloying elements on corrosion of Ni-based alloys in NaCl-KCl-MgCl2 under Ar in the temperature range of 600 similar to 800 degrees C were investigated by immersion test, SEM/EDS, EPMA and XRD techniques. A thermodynamic potential-pO(2-) diagram for Cr, Ni at 700 degrees C was constructed. The alloy corrosion is attributed to the dissolution of Cr to form Cr chlorides into salt. The elements Cr, Mo and W can affect the alloy corrosion. The corrosion is accelerated and the intergranular corrosion becomes more pronounced with temperature. Furthermore, the effects of the alloying elements on corrosion have a strong temperature dependence. The related mechanisms are discussed. |
| 语种 | 英语 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/30917]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 作者单位 | Chinese Acad Sci, Shanghai Inst Appl Phys, 2019 Jialuo Rd, Shanghai 201800, Peoples R China |
| 推荐引用方式 GB/T 7714 | Sun, H,Zhang, P,Wang, JQ. Effects of alloying elements on the corrosion behavior of Ni-based alloys in molten NaCl-KCl-MgCl(2 )salt at different temperatures[J]. CORROSION SCIENCE,2018,143(-):187-199. |
| APA | Sun, H,Zhang, P,&Wang, JQ.(2018).Effects of alloying elements on the corrosion behavior of Ni-based alloys in molten NaCl-KCl-MgCl(2 )salt at different temperatures.CORROSION SCIENCE,143(-),187-199. |
| MLA | Sun, H,et al."Effects of alloying elements on the corrosion behavior of Ni-based alloys in molten NaCl-KCl-MgCl(2 )salt at different temperatures".CORROSION SCIENCE 143.-(2018):187-199. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。