Great structural stability of irradiated graphite after testing in molten Li2BeF4 salt
文献类型：期刊论文
| 作者 | Huang, Q; Tang, H |
| 刊名 | NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS
 |
| 出版日期 | 2018 |
| 卷号 | 436期号:-页码:40-44 |
| 关键词 | ION-IRRADIATION PROTON IRRADIATION RAMAN-SPECTRA IG-110 |
| ISSN号 | 0168-583X |
| DOI | 10.1016/j.nimb.2018.08.049 |
| 文献子类 | 期刊论文 |
| 英文摘要 | One IG-110 graphite sample was irradiated with 2 MeV Xe20+ ions to a fluence of 2.4 x 10(15) ions/cm(2). Then the irradiated sample and one un-irradiated sample were tested in molten Li2BeF4 salt at a pressure of 0.3 MPa for 20 h, in order to investigate irradiation's effects on graphite-Li2BeF4 salt compatibility. For both samples, the intruded salt have round surfaces and spherical salt particles with sizes < 2 mu m were shown on samples' surface, indicating that irradiation did not change the non-wettability of Li2BeF4 salt to graphite. Besides, testing in molten Li2BeF4 salt did not have obvious effects on graphite's surface morphology and Raman peaks, indicating that chemical attack did not happen to irradiated graphite. Therefore, irradiated graphite has a great structural stability in molten Li2BeF4 salt. |
| 语种 | 英语 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/30960]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 作者单位 | Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China |
| 推荐引用方式 GB/T 7714 | Huang, Q,Tang, H. Great structural stability of irradiated graphite after testing in molten Li2BeF4 salt[J]. NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS,2018,436(-):40-44. |
| APA | Huang, Q,&Tang, H.(2018).Great structural stability of irradiated graphite after testing in molten Li2BeF4 salt.NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS,436(-),40-44. |
| MLA | Huang, Q,et al."Great structural stability of irradiated graphite after testing in molten Li2BeF4 salt".NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS 436.-(2018):40-44. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。