Effects of He ion irradiation on the corrosion performance of alloy GH3535 welded joint in molten FLiNaK
文献类型：期刊论文
| 作者 | Liu, M; Hou, J; Han, FF; Liu, RD; Zhou, XT |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2019 |
| 卷号 | 146期号:-页码:172—178 |
| 关键词 | MO-CR ALLOY TEMPERATURE BUBBLES |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2018.10.038 |
| 文献子类 | 期刊论文 |
| 英文摘要 | In present study, the influence of He irradiation on the corrosion performance of a GH3535 welded joint has been investigated. A welded joint was irradiated with 300 keV He ions and corroded in FLiNaK molten salt at 700 degrees C for 400 h. The microstructures after corrosion were characterized by SEM, EPMA and TEM. The corrosion produced cavities and created Cr depletion. He bubbles were formed and grew during corrosion. Although He irradiation did not obviously deteriorate corrosion-induced Cr depletion, the combination effect of He bubbles and corrosion attack caused severe damage to the joint, enlarging bubbles and/or cavities into large holes. |
| 语种 | 英语 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/31577]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 作者单位 | 1.Univ Shanghai Sci & Technol, Sch Mat Sci & Engn, Shanghai 200093, Peoples R China 2.Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China; |
| 推荐引用方式 GB/T 7714 | Liu, M,Hou, J,Han, FF,et al. Effects of He ion irradiation on the corrosion performance of alloy GH3535 welded joint in molten FLiNaK[J]. CORROSION SCIENCE,2019,146(-):172—178. |
| APA | Liu, M,Hou, J,Han, FF,Liu, RD,&Zhou, XT.(2019).Effects of He ion irradiation on the corrosion performance of alloy GH3535 welded joint in molten FLiNaK.CORROSION SCIENCE,146(-),172—178. |
| MLA | Liu, M,et al."Effects of He ion irradiation on the corrosion performance of alloy GH3535 welded joint in molten FLiNaK".CORROSION SCIENCE 146.-(2019):172—178. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。