Static recrystallization of transparent polycrystalline yttrium aluminum garnet (YAG)
文献类型:期刊论文
作者 | Jiang, Wen; Cheng, Xingwang; Xiong, Zhiping; Cai, Hongnian; Zhang, Jian |
刊名 | SCRIPTA MATERIALIA |
出版日期 | 2019-12-01 |
卷号 | 173页码:37 |
ISSN号 | 1359-6462 |
关键词 | Yttrium aluminum garnet (YAG) Cold-working Recrystallization |
DOI | 10.1016/j.scriptamat.2019.07.047 |
文献子类 | Article |
英文摘要 | Cold deformation was realized in the transparent polycrystalline yttrium aluminum garnet (YAG) using Vickers indentation. Following this, annealing at 1500 degrees C for 2 h led to a grain refinement from 4.8 to 0.49 mu m in the plastically deformed region, indicating the occurrence of recrystallization. It is supported by transmission electron microscope characterization that plastic deformation-induced dislocations are annihilated and rearranged, resulting in the formation of new grain boundaries during annealing. (C) 2019 Acta Materialia Inc Published by Elsevier Ltd. All rights reserved. |
WOS研究方向 | Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
源URL | [http://ir.sic.ac.cn/handle/331005/26722] |
专题 | 中国科学院上海硅酸盐研究所 |
推荐引用方式 GB/T 7714 | Jiang, Wen,Cheng, Xingwang,Xiong, Zhiping,et al. Static recrystallization of transparent polycrystalline yttrium aluminum garnet (YAG)[J]. SCRIPTA MATERIALIA,2019,173:37. |
APA | Jiang, Wen,Cheng, Xingwang,Xiong, Zhiping,Cai, Hongnian,&Zhang, Jian.(2019).Static recrystallization of transparent polycrystalline yttrium aluminum garnet (YAG).SCRIPTA MATERIALIA,173,37. |
MLA | Jiang, Wen,et al."Static recrystallization of transparent polycrystalline yttrium aluminum garnet (YAG)".SCRIPTA MATERIALIA 173(2019):37. |
入库方式: OAI收割
来源:上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。