High strength polymer/silicon nitride composites for dental restorations
文献类型:期刊论文
作者 | Wang, Feng; Guo, Jingshu; Li, Ke; Sun, Jian; Zeng, Yuping; Ning, Congqin |
刊名 | DENTAL MATERIALS |
出版日期 | 2019-09-01 |
卷号 | 35期号:9页码:1254 |
ISSN号 | 0109-5641 |
关键词 | Porous Si3N4 Polymer-infiltrated Si3N4 composites Dental restoration Cytocompatibility |
DOI | 10.1016/j.dental.2019.05.022 |
文献子类 | Article |
英文摘要 | Objectives. To fabricate polymer-infiltrated silicon nitride composite (PISNC) and evaluate the potential of PISNC in dental application. Methods. Porous silicon nitride (Si3N4) ceramics were fabricated through gelcasting and pressureless sintering. Polymer infiltrating was carried out then and composites were obtained after curing of polymer. Flexural strength and microstructures of porous ceramic scaffolds and polymer-infiltrated composites were obtained by three-point bending and SEM, respectively. Phase distributions of polymer-infiltrated ceramics were observed by EDS. Human gingival fibroblast cells (HGFs) were used to evaluate the cytocompatibility and IL-6 release. The cell morphology were observed by SEM. The amount of released IL-6 was investigated using ELISA test system. Results. Porosity and mechanical strength of porous ceramics ranged from 45.1 to 49.3% and 171.8-262.3 MPa, respectively. The bicontinuous structure of polymer-infiltrated composites possessed them with excellent mechanical properties. Porosity and mechanical strength of polymer-infiltrated Si3N4 composites ranged from 1.94 to 2.28% and 273-385.3 MPa, respectively. Additionally, the PISNC enhanced the initial adhesion and spreading activity of HGFs compared with PMMA. The PISNC showed similar IL-6 release performance with PMMA samples. Significances. The PISNC is a promising candidate for dental restorations and high-load medical applications. (C) 2019 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved. |
WOS研究方向 | Dentistry, Oral Surgery & Medicine ; Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
源URL | [http://ir.sic.ac.cn/handle/331005/26873] |
专题 | 中国科学院上海硅酸盐研究所 |
推荐引用方式 GB/T 7714 | Wang, Feng,Guo, Jingshu,Li, Ke,et al. High strength polymer/silicon nitride composites for dental restorations[J]. DENTAL MATERIALS,2019,35(9):1254. |
APA | Wang, Feng,Guo, Jingshu,Li, Ke,Sun, Jian,Zeng, Yuping,&Ning, Congqin.(2019).High strength polymer/silicon nitride composites for dental restorations.DENTAL MATERIALS,35(9),1254. |
MLA | Wang, Feng,et al."High strength polymer/silicon nitride composites for dental restorations".DENTAL MATERIALS 35.9(2019):1254. |
入库方式: OAI收割
来源:上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。