A simple way to prepare Co:MgAl2O4 transparent ceramics for saturable absorber
文献类型：期刊论文
| 作者 | Su, Sha; Liu, Qiang; Hu, Zewang; Chen, Xiaopu; Pan, Hongming; Liu, Xin; Wu, Lexiang; Li, Jiang |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2019-08-15 |
| 卷号 | 797页码:1288 |
| ISSN号 | 0925-8388 |
| 关键词 | Co:MgAl2O4 Transparent ceramics Saturable absorbers Hot isostatic pressing |
| DOI | 10.1016/j.jallcom.2019.04.322 |
| 文献子类 | Article |
| 英文摘要 | Co-doped magnesium aluminate (Co:MgAl2O4) transparent ceramics were obtained by pre-sintering in air and hot isostatic pressing (HIP) with commercial spinel and CoO powders as raw materials. The influences of the pre-sintering temperature on the microstructure and optical quality of the 0.05 at% Co:MgAl2O4 ceramics were studied. It is found that the relative density of Co:MgAl2O4 ceramics increases from 96.8% at 1500 degrees C to 98.7% at 1600 degrees C and then decreases with further increasing the pre-sintering temperature. The average grain size of Co:MgAl2O4 ceramics increase from 4.6 mm to 19.2 mu m with the increase of pre-sintering temperature from 1500 to 1700 degrees C. For the sample pre-sintered at 1600 degrees C for 5 h and HIP post-treated at 1800 degrees C for 3 h, the average grain size is about 23.0 mm and the near in-line transmittance reaches 75% at the wavelength range of 1700-2400 nm. The ground state absorption cross section at 1540 nm of the optimal 0.05 at% Co:MgAl2O4 ceramics is calculated to be 2.9 x 10 x 19 cm(2). (C) 2019 Published by Elsevier B.V. |
| WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | ELSEVIER SCIENCE SA |
| 源URL | [http://ir.sic.ac.cn/handle/331005/26909]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Su, Sha,Liu, Qiang,Hu, Zewang,et al. A simple way to prepare Co:MgAl2O4 transparent ceramics for saturable absorber[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2019,797:1288. |
| APA | Su, Sha.,Liu, Qiang.,Hu, Zewang.,Chen, Xiaopu.,Pan, Hongming.,...&Li, Jiang.(2019).A simple way to prepare Co:MgAl2O4 transparent ceramics for saturable absorber.JOURNAL OF ALLOYS AND COMPOUNDS,797,1288. |
| MLA | Su, Sha,et al."A simple way to prepare Co:MgAl2O4 transparent ceramics for saturable absorber".JOURNAL OF ALLOYS AND COMPOUNDS 797(2019):1288. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。