Fabrication and laser operation of Yb:Lu2O3 transparent ceramics from co-precipitated nano-powders
文献类型：期刊论文
| 作者 | Liu, Ziyu; Toci, Guido; Pirri, Angela; Patrizi, Barbara; Li, Jinbang; Hu, Zewang; Wei, Jiabei; Pan, Hongming; Xie, Tengfei; Vannini, Matteo |
| 刊名 | JOURNAL OF THE AMERICAN CERAMIC SOCIETY
 |
| 出版日期 | 2019-12-01 |
| 卷号 | 102期号:12页码:7491 |
| 关键词 | co-precipitation method hot isostatic pressing laser performance microstructure Yb Lu2O3 transparent ceramics |
| ISSN号 | 0002-7820 |
| DOI | 10.1111/jace.16674 |
| 文献子类 | Article |
| 英文摘要 | In this article, 5 at.% Yb:Lu2O3 transparent ceramics were fabricated by vacuum sintering combined with hot isostatic pressing (HIP) posttreatment using co-precipitated nano-powders. The influence of precipitant molar ratio, ammonium hydrogen carbonate, to metal ions (AHC/M3+, R value) on the properties of Yb:Lu2O3 precursors and calcined powders was investigated systematically. It was found that the powders with different R value calcined at 1100 degrees C for 4 hours were pure cubic Lu2O3 but the morphologies of precursors and powders behaved differently. The opaque samples pre-sintered at 1500 degrees C for 2 hours grew into transparent ceramics after HIP posttreatment at 1750 degrees C for 1 hour. The final ceramic with R = 4.8 showed the best optical quality with the in-line transmittance of 79.7% at 1100 nm. The quasi-CW laser operation was performed at 1034 nm and 1080 nm with a maximum output power up to 8.15 W as well as a corresponding slope efficiency of 58.4%. |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| 出版者 | WILEY |
| 源URL | [http://ir.sic.ac.cn/handle/331005/26982]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 推荐引用方式 GB/T 7714 | Liu, Ziyu,Toci, Guido,Pirri, Angela,et al. Fabrication and laser operation of Yb:Lu2O3 transparent ceramics from co-precipitated nano-powders[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2019,102(12):7491. |
| APA | Liu, Ziyu.,Toci, Guido.,Pirri, Angela.,Patrizi, Barbara.,Li, Jinbang.,...&Li, Jiang.(2019).Fabrication and laser operation of Yb:Lu2O3 transparent ceramics from co-precipitated nano-powders.JOURNAL OF THE AMERICAN CERAMIC SOCIETY,102(12),7491. |
| MLA | Liu, Ziyu,et al."Fabrication and laser operation of Yb:Lu2O3 transparent ceramics from co-precipitated nano-powders".JOURNAL OF THE AMERICAN CERAMIC SOCIETY 102.12(2019):7491. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。